Effect of (Ti0.35V0.65)0.86Fe0.14Hy on synthesis and hydrogen storage properties of NaAlH4
Ya-Dong Wang,Chang-Run Li,Jia-Bao Wen,Wei-He Meng,Ke Wang,Sen-Miao Zhao,Hai-Zhen Liu,Cun-Ke Huang,Jin Guo
DOI: https://doi.org/10.1016/j.ijhydene.2023.01.207
IF: 7.2
2023-02-01
International Journal of Hydrogen Energy
Abstract:The (Ti0 . 35V0.65)0.86Fe0.14Hy powder was prepared by melting, annealing and H2-assisted-crushed method to avoid passivation. Then [(Ti0 . 35V0.65)0.86Fe0.14Hy]x/100-NaAlH4 composite system were synthesized using a two-step in-situ-milling method with the proportion of n (NaH):n (Al):n (Graphene):n (alloy) = 100:100:5:x (x = 2,5,8). It was found that lattice distortion had occurred on the alloy after 190hindividually milling, and the hydrogen storage capacity had decreased significantly to 1.10 wt%. However, after long-term composite milling, the alloy could still reduce the hydrogen pressure required for the synthesis of NaAlH4, besides it could effectively reduce the hydriding/dehydriding temperature and improve the kinetic properties. This may due to the alloy's ability to dissociate H2 and transfer H at room temperature, thereby enhancing the opportunity for direct contact between the matrix and H. In this study, x = 5 was the optimal alloy addition ratio, its dehydrogenation capacity at the 1st cycle reached 5.04 wt%; and at the 2nd and subsequent cycles, it remained rather stable at 4.40 wt%.
energy & fuels,electrochemistry,chemistry, physical