Abstract:Porous activated carbon with a ultrahigh specific surface area (3164 m2 g−1) and large pore volume (1.88 cm3 g−1) was prepared from waste litchi shells with channel-like macropores via a KOH activation method. The macroporous structure of litchi shells is believed to be conducive to distribute the activation agent, which enables sufficient activation. The as-prepared activated carbon was developed as a conducting framework for lithium–sulfur battery cathode materials. The resulting activated carbon/sulfur composite cathode possesses a high specific capacity, good rate capability, and long-term cycling performance. At 200 mA g−1 current density, the initial discharge capacity of the activated carbon/sulfur composite cathode with 60 wt% sulfur content is 1105 mA h g−1. At a current density of 800 mA g−1, the activated carbon/sulfur composite cathode shows 51% capacity retention over 800 cycles with a fade rate of 0.06% per cycle. The coulombic efficiency of the cell remains at approximately 95%. By adding LiNO3 in the electrolyte, the activated carbon/sulfur composite electrode tested at 800 mA g−1 shows a high coulombic efficiency (>99%). The activated carbon/sulfur composites exhibited similar capacity value and cycling trends with an increase in sulfur content from 60% to 68%. The good electrochemical performance can be attributed to the excellent structural parameters of the activated carbon. The ultrahigh specific surface area and large pore volume not only enhances the sulfur content but also ensures dispersion of elemental sulfur in the conducting framework, thereby improving sulfur utilization. The small nanopores of the activated carbon can effectively inhibit the diffusion of polysulfides during the charge/discharge process.

High Sulfur Loading in Activated Bamboo-Derived Porous Carbon As a Superior Cathode for Rechargeable Li–S Batteries

Natural Okra Shells Derived Nitrogen‐Doped Porous Carbon to Regulate Polysulfides for High‐Performance Lithium–Sulfur Batteries

Microporous Bamboo Biochar for Lithium-Sulfur Batteries

Hierarchically Structured Sulfur/Carbon Nanocomposite Material for High-Energy Lithium Battery

Biomass-Derived Activated Carbon for Rechargeable Lithium-Sulfur Batteries

Activated Carbon with Ultrahigh Specific Surface Area Synthesized from Natural Plant Material for Lithium–sulfur Batteries

Biomass-Derived Carbon for High-Performance Lithium-Sulfur Batteries

Porous Coconut Shell Carbon Offering High Retention and Deep Lithiation of Sulfur for Lithium-Sulfur Batteries

Hierarchical Porous Carbon Materials Derived from Self-Template Bamboo Leaves for Lithium–Sulfur Batteries

Built‐in Carbon Nanotube Network Inside a Biomass‐Derived Hierarchically Porous Carbon to Enhance the Performance of the Sulfur Cathode in a Li‐S Battery

Green biomass-derived hierarchically porous non-activated carbon from carob waste for high-performance lithium-sulfur batteries

Biomass-Derived Porous Carbon with Micropores and Small Mesopores for High-Performance Lithium-Sulfur Batteries

Biomass Waste Inspired Highly Porous Carbon for High Performance Lithium/Sulfur Batteries

Optimized Assembly of Micro-/Meso-/Macroporous Carbon for Li–S Batteries

High specific surface area bimodal porous carbon derived from biomass reed flowers for high performance lithium-sulfur batteries

Optimized Sulfur-Loading in Nitrogen-Doped Porous Carbon for High-Capacity Cathode of Lithium–sulfur Batteries

Metal-Embedded Porous Graphitic Carbon Fibers Fabricated from Bamboo Sticks As a Novel Cathode for Lithium-Sulfur Batteries

Atomic-Layer-Deposition Functionalized Carbonized Mesoporous Wood Fiber for High Sulfur Loading Lithium Sulfur Batteries

A hierarchical micro/mesoporous carbon fiber/sulfur composite for high-performance lithium-sulfur batteries

Preparation of activated carbon derived from biomass and its application in lithium–sulfur batteries

Porous 3D graphene-based biochar materials with high areal sulfur loading for lithium–sulfur batteries