Nano-modified functional composite coatings for metallic structures: Part II—Mechanical and damage tolerance
Xingyu Wang,Fujian Tang,Qi Cao,Xiaoning Qi,Hong Pan,Zhibin Lin,Dante Battocchi
DOI: https://doi.org/10.1016/j.surfcoat.2020.126274
IF: 4.865
2020-11-01
Surface and Coatings Technology
Abstract:<p>While corrosion resistance of protective coatings is often defined as one critical property for corrosion mitigation, damage resistance is another crucial parameter in the design of coatings. Low damage tolerance of polymer coatings often leads to premature failure and eventually result in a shortened service life. Thus, a high-performance protective layer must be synthesized with the desired function of mechanical and damage corrosion, as well as corrosion resistance. The study was intended to provide a thorough understanding of the mechanical properties, characterization, and damage resistance of the nanocomposite coatings under three different nanofillers, nanosilica (NS), carbon nanotubes (CNT), and graphene nanoplatelets (GNP). The research results demonstrated that the nanocomposites reinforced by different nanoparticles exhibited improved Young's modulus, tensile strength, and ultimate strain. Specifically, the composites had considerable improvement in their tensile strength and stiffness. The 1.0 wt% CNT-epoxy composites had the highest increase in their tensile strength and Young's modulus, by 53% and 34%, respectively, over the neat epoxy. Meanwhile, the NS reinforced composites displayed the higher ductility over their counterparts and the 1.5 wt% of NS-epoxy samples had an increase in their ultimate strain, by 37% of the neat epoxy. A similar trend of enhanced abrasive resistance and improved adhesive capability was observed in CNT-epoxy groups, where over 40% increase in abrasion resistance as compared to the neat epoxy was observed; thus, the 44% improvement was observed in pull-off strength. All composite coatings had no apparent increase in wettability, where atomic force microscope (AFM) images confirmed that the inclusion of nanoparticles reduced the surface roughness of the nanocomposites.</p>
physics, applied,materials science, coatings & films