Tongle Bu,Jing Li,Qingdong Lin,David P. McMeekin,Jingsong Sun,Mingchao Wang,Weijian Chen,Xiaoming Wen,Wenxin Mao,Christopher R. McNeill,Wenchao Huang,Xiao-Li Zhang,Jie Zhong,Yi-Bing Cheng,Udo Bach,Fuzhi Huang
DOI: https://doi.org/10.1016/j.nanoen.2020.104917
IF: 17.6
2020-09-01
Nano Energy
Abstract:<p>Wide bandgap perovskite solar cells (PSCs) are a key component for the realization of highly efficient tandem solar cells. To simultaneously improve the efficiency and stability is still a big challenge. Herein, phenylmethylamine bromide (PMABr) is employed to modify FA<sub>0.8</sub>Cs<sub>0.2</sub>Pb(I<sub>0.7</sub>Br<sub>0.3</sub>)<sub>3</sub> wide bandgap perovskite films. This large cation is incorporated via a post-treatment, which induces a hierarchical layered perovskite and passivates the halide vacancies with the added Br<sup>−</sup>. The morphology of post-treated films is investigated with synchrotron-based techniques, revealing the formation of a layered structure at the surface, which depends upon the concentration of the PMABr solution. In particular a hierarchical microstructure is observed, consisting of a highly stable pure 2D (n = 1) perovskite layer on top of an efficient quasi-2D (n = 2) perovskite layer that caps an underlying 3D perovskite film. By precisely controlling the surface structure and thickness of the 2D perovskites, wide bandgap (~1.74 eV) PSCs reach an efficiency of 18.5% with negligible hysteresis and a stabilized efficiency of 17.9%. Furthermore, the device moisture stability is also significantly enhanced after the post-treatment, indicating that the post-treatment with PMABr is a viable processing method to achieve both efficient and stable wide bandgap PSCs.</p>
materials science, multidisciplinary,chemistry, physical,physics, applied,nanoscience & nanotechnology