Abstract:Solid oxide fuel cell directly and efficiently converts chemical energy to electrical energy. However, the necessity for high operating temperatures can result in mechanical failure. Fuel cell is a multilayer system and its stress distribution is greatly affected by the interface morphology. In this work, cosine interfaces with different amplitudes are used to approximate the fluctuation of actual interface. The effects of interface morphology on stress state, energy release rate of crack and creep behavior have been investigated. The results show that if the interface is planar, the residual normal stress component is zero on the interface, while the nonplanarity of interface can cause the normal stress S-n and shear stress S-t on the interface. When the amplitude is relatively small, the max values of S-n and S-t on the interfaces vary linearly with increasing amplitudes in both anode and cathode. Above a certain value, nonlinearity of the interface becomes important. Max tensile S-n always occurs at the peak of convex interface, but the position of max compressive S-n varies. Max shear stress is prone to occur at 1/4 of the wavelength at small amplitude and moves towards 1/2 of the wavelength when the amplitude increases. Fracture mechanics analysis shows that the surface crack possibly penetrates into the anode function layer and then is constrained by the stiff electrolyte. On the other hand, the horizontal crack likely penetrates into the electrolyte layer when the interface is not planar. Creep analysis shows that 11 800 hours of continuous operation at high temperature cannot remove stress undulation introduced by nor-planar interface but can make max value of Sn and St decrease around 30%.

Effect of Temperature Fluctuation on Creep and Failure Probability for Planar Solid Oxide Fuel Cell

Effect of Operating Temperature on Creep and Damage in the Bonded Compliant Seal of Planar Solid Oxide Fuel Cell

Mismatch effect of material creep strength on creep damage and failure probability of planar solid oxide fuel cell

High temperature creep strength design and optimization of solid oxide fuel cell

Creep Analysis of Solid Oxide Fuel Cell with Bonded Compliant Seal Design

Solid Oxide Electrolysis Cell under Real Fluctuating Power Supply with a Focus on Thermal Stress Analysis

Study on creep damage and life prediction of the planar solid oxide fuel cell by modeling of multiphysics coupled

Numerical Study on the Mechanical Stress and Mechanical Failure of Planar Solid Oxide Fuel Cell

Effects of a cooling channel on the creep damage and failure probability of planar solid oxide fuel cells

Time Dependent Failure Probability Estimation of the Solid Oxide Fuel Cell by a Creep-Damage Related Weibull Distribution Model

Effect of the Geometrical Size on Time Dependent Failure Probability of the Solid Oxide Fuel Cell

Evolution of Thermal Stress and Failure Probability During Reduction and Re Oxidation of Solid Oxide Fuel Cell

Long-term thermo-mechanical performance evolution of a 15-cell solid oxide fuel cell stack

Long-term Evolution of Mechanical Performance of Solid Oxide Fuel Cell Stack and the Underlying Mechanism

Investigation of creep damage and failure probability in solid oxide fuel cells with different flow channel geometries

Using Short-Time Creep Relaxation Effect to Decrease the Residual Stress in the Bonded Compliant Seal of Planar Solid Oxide Fuel Cell – A Finite Element Simulation

Thermo-Electro-Chemo-Mechanical Modeling of Solid Oxide Fuel Cell for Stress and Failure Evolution During Duty Cycle

Effect of Inhomogeneous Oxidation on the Mechanical Degradation of Anode Supported Solid Oxide Fuel Cell

Effect of Frame Material on the Creep of Solid Oxide Fuel Cell

Thermal Shock Resistance and Failure Probability Analysis on Solid Oxide Electrolyte Direct Flame Fuel Cells

Effect of Interface Morphology on the Residual Stress Distribution in Solid Oxide Fuel Cell