Abstract:The hydrothermal synthesis of ZnO nanorods (NRs) has been investigated using ammonium hydroxide and polyethyleneimine as additives to the conventional nitrate based synthesis route, to obtain thin-films of well-aligned, ultradense and ultralong nanostructures. ZnO NRs longer than 60 μm were obtained in a one-cycle growth run and rod lengths ~ 100 μm by a two-cycle growth. The lengths of the rods were distributed uniformly across the substrate in all samples and highly dense NR arrays were observed. These conditions were obtained by a careful review of the nucleation and growth kinetics for this material system, such that the supersaturation of the solution was only relieved by precipitation on and in the presence of crystalline ZnO, and by the exploitation of a second growth phase due to the chelating behave of PEI and the products of HMTA. Also, the growth behavior was correlated to the solution pH values. The structural and optical data were found to be supportive of the growth conditions. The photoluminescence (PL) spectra from as-grown ultralong ZnO NRs exhibited a strong broad (580-625 nm) visible emission peak. However, annealing in a forming gas atmosphere at 623K (350°C) revealed a PL spectrum with a significantly decreased visible emission and an increased near band gap UV emission at 379 nm. Thus, the mechanisms associated with ammonium hydroxide and PEI addition provide a simple route for synthesizing ultralong and dense arrays of ZnO NRs at low temperature i.e. 368K (95°C).

Synthesis of Vertical Arrays of Ultra Long ZnO Nanowires on Noncrystalline Substrates

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Arrays of ZnO Nanowires Fabricated by a Simple Chemical Solution Route

Low-temperature Growth and Raman Scattering Study of Vertically Aligned ZnO Nanowires on Si Substrate

Growth of Arrayed ZnO Nanowires Using a Solution Method

Alignment-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

On the formation of well-aligned ZnO nanowall networks by catalyst-free thermal evaporation method

Carbon-Assisted Synthesis of Aligned Zno Nanowires

Synthesis of Well-aligned ZnO Nanowires Using Simple Physical Vapor Deposition Without Catalysts or Additives

Layer-by-layer Growth of Ultralong ZnO Vertical Wire Arrays for Enhanced Photoelectrocatalytic Activity

Growth mechanism and diameter control of well-aligned small-diameter ZnO nanowire arrays synthesized by a catalyst-free thermal evaporation method.

Facile and Controllable Growth of ZnO 1D Nanostructure Arrays on Zn Substrate by Hydrothermal Process

A New Method for Bulk-Quantity Synthesis of Patterned Well-Aligned Zno Nanowire Arrays

Ultra-fast microwave-assisted hydrothermal synthesis of long vertically aligned ZnO nanowires for dye-sensitized solar cell application

Low temperature growth and properties of ZnO nanorod arrays

Systematic study of vertically aligned ZnO nanowire arrays synthesized on p-GaN substrate by hydrothermal method

Large-Scale Synthesis of Bicrystalline ZnO Nanowire Arrays by Thermal Oxidation of Zinc Film: Growth Mechanism and High-Performance Field Emission

Improved seedless hydrothermal synthesis of dense and ultralong ZnO nanowires.

Large-Scale and Rapid Synthesis of Ultralong ZnO Nanowire Films via Anodization

Catalyst-free Synthesis of Well-Aligned ZnO Nanowires on In0.2Ga0.8N, GaN, and Al0.25Ga0.75N Substrates.

Low-temperature hydrothermally grown 100 μm vertically well-aligned ultralong and ultradense ZnO nanorod arrays with improved PL property