Abstract:Well-aligned small-diameter ZnO nanowire arrays have been synthesized on Si wafers pre-coated with c-oriented ZnO thin films by a catalyst-free thermal evaporation method. The morphology of the products has been found to be greatly affected by the oxygen flow rate. The self-catalyzed VLS mechanism is proposed to interpret the growth of the ZnO nanowires and the change in the product morphology. Classical nucleation theory is employed to analyze the growth process of the ZnO nanowires, and Zn vapor supersaturation is proposed to be a key factor to affect the diameter and the areal density of the ZnO nanowires. The average diameter of the ZnO nanowires can be finely controlled in the range of 12-31 nm by controlling the oxygen flow rate and hence the Zn vapor supersaturation. This result is consistent with our theoretical prediction. X-ray photoelectron spectroscopy measurements were performed to characterize the stoichiometry of nanowires with various average diameters. It also revealed that there are many OH species on the nanowire surface. Photoluminescence measurements showed that the deep-level emission of the nanowires with average diameter of 12 nm peaks in the yellow region, which may be attributed to the presence of OH species and surface effects.

Synthesis of Well-aligned ZnO Nanowires Using Simple Physical Vapor Deposition Without Catalysts or Additives

Synthesis of Well-Aligned Zno Nanowires Without Catalysts

On the formation of well-aligned ZnO nanowall networks by catalyst-free thermal evaporation method

Catalyst-free Synthesis of Well-Aligned ZnO Nanowires on In0.2Ga0.8N, GaN, and Al0.25Ga0.75N Substrates.

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Carbon-Assisted Synthesis of Aligned Zno Nanowires

Synthesis and Optical Properties of Well-Aligned ZnO Nanorod Array on an Undoped ZnO Film

Well-aligned ZnO Nanowires Grown on Si Substrate Via Metal–organic Chemical Vapor Deposition

Growth And Characterization Of Cu-Catalyzed Zno Nanowires

Growth mechanism and diameter control of well-aligned small-diameter ZnO nanowire arrays synthesized by a catalyst-free thermal evaporation method.

Synthesis and Characterization of ZnO Nanowires Using a Simple PVD Approach Without Catalysts

Well-Aligned Zno Nanocolumns Grown by Reactive Electron Beam Evaporation

Arrays of ZnO Nanowires Fabricated by a Simple Chemical Solution Route

Rapid Synthesis of Aligned Zinc Oxide Nanowires.

Synthesis and Electrical Properties of ZnO Nanowires

Metal-catalyst-free epitaxial growth of aligned ZnO nanowires on silicon wafers at low temperature

Preparation and Photoluminescence of ZnO with Nanostructure by Hollow-Cathode Discharge

Synthesis and electrical properties of ZnO nanowires.

Low-temperature Growth and Raman Scattering Study of Vertically Aligned ZnO Nanowires on Si Substrate

Growth of Arrayed ZnO Nanowires Using a Solution Method

Aligned growth of ZnO nanowires by NAPLD and their optical characterizations