Abstract:The hydrothermal synthesis of ZnO nanorods (NRs) has been investigated using ammonium hydroxide and polyethyleneimine as additives to the conventional nitrate based synthesis route, to obtain thin-films of well-aligned, ultradense and ultralong nanostructures. ZnO NRs longer than 60 μm were obtained in a one-cycle growth run and rod lengths ~ 100 μm by a two-cycle growth. The lengths of the rods were distributed uniformly across the substrate in all samples and highly dense NR arrays were observed. These conditions were obtained by a careful review of the nucleation and growth kinetics for this material system, such that the supersaturation of the solution was only relieved by precipitation on and in the presence of crystalline ZnO, and by the exploitation of a second growth phase due to the chelating behave of PEI and the products of HMTA. Also, the growth behavior was correlated to the solution pH values. The structural and optical data were found to be supportive of the growth conditions. The photoluminescence (PL) spectra from as-grown ultralong ZnO NRs exhibited a strong broad (580-625 nm) visible emission peak. However, annealing in a forming gas atmosphere at 623K (350°C) revealed a PL spectrum with a significantly decreased visible emission and an increased near band gap UV emission at 379 nm. Thus, the mechanisms associated with ammonium hydroxide and PEI addition provide a simple route for synthesizing ultralong and dense arrays of ZnO NRs at low temperature i.e. 368K (95°C).

Low temperature growth and properties of ZnO nanorod arrays

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Low Temperature Synthesis and Optical Properties of Small-Diameter ZnO Nanorods

Effect of UV irradiation on the properties of ZnO nanorod arrays prepared by hydrothermal method

A Simple and Novel Low-Temperature Hydrothermal Synthesis of ZnO Nanorods

Low-temperature hydrothermally grown 100 μm vertically well-aligned ultralong and ultradense ZnO nanorod arrays with improved PL property

Alignment-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

Fabrication of oriented ZnO nanorod arrays and their optical performances

Growth of flower-like ZnO on ZnO nanorod arrays created on zinc substrate through low-temperature hydrothermal synthesis

Low-temperature growth of uniform ZnO particles with controllable ellipsoidal morphologies and characteristic luminescence patterns.

Straight and Thin ZnO Nanorods: Hectogram-Scale Synthesis at Low Temperature and Cathodoluminescence.

Low-Temperature Growth and Properties of Zno Nanowires

Synthesis and Optical Properties of Well-Aligned ZnO Nanorod Array on an Undoped ZnO Film

Facile and Controllable Growth of ZnO 1D Nanostructure Arrays on Zn Substrate by Hydrothermal Process

Growth And Characterization Of Cu-Catalyzed Zno Nanowires

A Novel Low-Temperature Method to Grow Single-Crystal Zno Nanorods

Fabrication and optical property of ZnO nanorod array by hydrothermal method

Room-temperature nonequilibrium growth of controllable ZnO nanorod arrays

Synthesis of aligned ZnO submicron rod arrays by heating zinc foil covered with ZnCl2 solution

Low-temperature synthesis of ZnO nanonails