Abstract:Zinc oxide (ZnO) has a wide direct band gap of 3.37 eV at room temperature and a large excitonic binding energy of 60 meV. In this work, ZnO nanoparticles had been successfully fabricated at low temperature (60 degrees C). The structures, morphologies and optical properties of ZnO nanoparticles were investigated by X-ray diffraction (XRD), a scanning electron microscope (SEM), UV-Visible absorption and photoluminescence (PL) spectra, respectively. Measurement results of XRD showed that the as-prepared ZnO nanoparticles are a random orientation. The nanoparticles are approximately particle shape with an average size of about 50 nm by SEM observation, UV-Vis absorption spectrum indicated that the as-prepared ZnO nanoparticles dispersed in chloroform are highly transparent in the visible region and have a strong absorption band in the UV region, at the same time, we found a sharp absorption edge at near 370 nm. In addition, in the as-prepared ZnO nanoparticles/chloroform solution, both a near band edge (NBE) ultraviolet photoluminescence peak at 372 nm and a defect related deep level emission (DLE) green peak at 513 nm were observed. It suggested that the NBE photoluminescence peak should be attributed to free excitons transition, the DLE green peak should be ascribed to intrinsic defects of the single ionized oxygen vacancy (V-o*) through our research results. Furthermore, we obtained R (R=I-NBE/I-DLE) value as 0.91. This indicates that there are a large amount of single ionized oxygen vacancies in as-prepared ZnO nanoparticles, which results in poor crystalline quality of ZnO nanoparticles.

Low Temperature Synthesis and Optical Properties of Small-Diameter ZnO Nanorods

A Simple and Novel Low-Temperature Hydrothermal Synthesis of ZnO Nanorods

Low temperature growth and properties of ZnO nanorod arrays

Low-Temperature Synthesis and Optical Property of ZnO Nanorod Arrays

Temperature-dependent Photoluminescence of ZnO Nanorods Prepared by a Simple Solution Route

Microstructure Characterization of Single-crystal ZnO Nanorods Synthesized by Solvothermal at Low Temperature

Photoluminescence Properties of ZnO Nanorods Prepared under Low Temperature

Synthesis at a Low Temperature and Optical Properties of ZnO Nanorods

Straight and Thin ZnO Nanorods: Hectogram-Scale Synthesis at Low Temperature and Cathodoluminescence.

Low Temperature Synthesis and Optical Properties of ZnO Nanowires

Low-temperature Growth and Optical Properties of ZnO Nanorods

Large-Scale Synthesis of Zno Nanowires Using A Low-Temperature Chemical Route and Their Photoluminescence Properties

Highly Monodispersed ZnO Nanorods: Preparation and Optical Properties

Growth of ZnO Nanoparticles at Low Temperature and Optical Properties

Hydrothermal Synthesis and Photoluminescent Properties of ZnO Nanorods

Low-temperature growth of uniform ZnO particles with controllable ellipsoidal morphologies and characteristic luminescence patterns.

Photoluminescence and Raman Scattering of ZnO Nanorods

Synthesis, optical and field electron emission properties of low-dimensional ZnO nano-structures

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

Synthesis of ZnO Nanorods by Wet-Chemical Method at Low Temperature

Low-temperature synthesis and characterization of ZnO quantum dots