Abstract:ZnO nanowires were successfully fabricated by using the hydrothermal method in the existence of the poly ethylene glycol (PEG) with the molecular weight of 200. The experimental results exhibit that the ZnO nanowires with the diameter of ~30nm and the length of ten micrometers. PL spectra show a weak ultraviolet emission and an intense broad visible emission band for as-grown and annealed samples. These visible emission bands exhibit red-shifts from green (545nm) to yellow (580nm) and blue-shifts from yellow (580nm) to green (520nm) by annealing at aerobic or anaerobic environment, it indicates that the defect types are changed by annealed at different environment. Additionally, the red-shifts (520nm) and blue-shifts (580) can match up the bimodal lorentzian fitting (520nm and 583nm) of as-growth, which suggest that the visible emission band (545nm) is closely related to oxygen defects. The oxygen atomic can enter into the crystal lattice of ZnO and decrease the oxygen vacancy in air or oxygen, whereas, more oxygen vacancy defects is gave rise in vacuum annealed. We guess the energy levels of the intrinsic defects in ZnO nanowire maybe like that: the electrons of Zni defects compound with holes of VZn, Oi and OZn levels and conform to the yellow emission, and the green emission corresponds to the electron transition from the association defects deep donor level to the valence band.

Synthesis and Photoluminescence of Aligned ZnO Nanorods by Thermal Decomposition of Zinc Acetate at a Substrate Temperature of ∼250 °C

Synthetic and Effect of Annealing on the Luminescent Properties of Zno Nanowire

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

Rod-Like Zinc Oxide Constructed by Nanoparticles: Synthesis, Characterization and Optical Properties

Low Temperature Synthesis and Optical Properties of Small-Diameter ZnO Nanorods

From Zinc Nanowires to Zinc Oxide Nanowires: A Low Substrate-Temperature Approach

Preparation and Photoluminescence of ZnO with Nanostructure by Hollow-Cathode Discharge

A Simple and Novel Low-Temperature Hydrothermal Synthesis of ZnO Nanorods

Temperature-dependent Photoluminescence of ZnO Nanorods Prepared by a Simple Solution Route

Low temperature growth and properties of ZnO nanorod arrays

Melting and Optical Properties of ZnO Nanorods

Preparation and photoluminescence of ZnO nanorods

On the formation of well-aligned ZnO nanowall networks by catalyst-free thermal evaporation method

Straight and Thin ZnO Nanorods: Hectogram-Scale Synthesis at Low Temperature and Cathodoluminescence.

Thermal-desorption Induced Enhancement and Patterning of Ultraviolet Emission in Chemically Grown ZnO

Low-temperature growth of uniform ZnO particles with controllable ellipsoidal morphologies and characteristic luminescence patterns.

Large-Scale Synthesis of Zno Nanowires Using A Low-Temperature Chemical Route and Their Photoluminescence Properties

Catalyst-free Synthesis of ZnO Nanowire Arrays on Zinc Substrate by Low Temperature Thermal Oxidation

Synthesis of aligned ZnO submicron rod arrays by heating zinc foil covered with ZnCl2 solution

Synthesis and Characterization of Aligned ZnO Nanorods on Porous Aluminum Oxide Template.

Synthesis and Luminescent Property of Single-Crystal Zno Nanobelts by A Simple Low Temperature Evaporation Route