Abstract:ZnO nanowires were successfully fabricated by using the hydrothermal method in the existence of the poly ethylene glycol (PEG) with the molecular weight of 200. The experimental results exhibit that the ZnO nanowires with the diameter of ~30nm and the length of ten micrometers. PL spectra show a weak ultraviolet emission and an intense broad visible emission band for as-grown and annealed samples. These visible emission bands exhibit red-shifts from green (545nm) to yellow (580nm) and blue-shifts from yellow (580nm) to green (520nm) by annealing at aerobic or anaerobic environment, it indicates that the defect types are changed by annealed at different environment. Additionally, the red-shifts (520nm) and blue-shifts (580) can match up the bimodal lorentzian fitting (520nm and 583nm) of as-growth, which suggest that the visible emission band (545nm) is closely related to oxygen defects. The oxygen atomic can enter into the crystal lattice of ZnO and decrease the oxygen vacancy in air or oxygen, whereas, more oxygen vacancy defects is gave rise in vacuum annealed. We guess the energy levels of the intrinsic defects in ZnO nanowire maybe like that: the electrons of Zni defects compound with holes of VZn, Oi and OZn levels and conform to the yellow emission, and the green emission corresponds to the electron transition from the association defects deep donor level to the valence band.

Synthesis and Luminescent Property of Single-Crystal Zno Nanobelts by A Simple Low Temperature Evaporation Route

Synthetic and Effect of Annealing on the Luminescent Properties of Zno Nanowire

Large-Scale Synthesis of Zno Nanowires Using A Low-Temperature Chemical Route and Their Photoluminescence Properties

Preparation of ZnO Particle with Novel Nut-Like Morphology by Ultrasonic Pretreatment and Its Luminescence Property

Preparation of Large-Scale Highly Oriented Zno Noodle Arrays and Study on the Photoconductivity

Preparation and Photoluminescence of ZnO with Nanostructure by Hollow-Cathode Discharge

Synthesis, structure, and photoluminescence of Zn2SnO4 single-crystal nanobelts and nanorings

Synthesis of ZnO Nanobelts by Carbothermal Reduction and Their Photoluminescence Properties.

A Simple Method to Synthesize Single-Crystalline Zn2SnO4(ZTO) Nanowires and Their Photoluminescence Properties

Low-temperature growth of uniform ZnO particles with controllable ellipsoidal morphologies and characteristic luminescence patterns.

Low Temperature Synthesis and Optical Properties of Small-Diameter ZnO Nanorods

Low-Temperature Growth and Properties of Zno Nanowires

On the formation of well-aligned ZnO nanowall networks by catalyst-free thermal evaporation method

ZnO Nanobelt Arrays Grown Directly from and on Zinc Substrates: Synthesis, Characterization, and Applications

Straight and Thin ZnO Nanorods: Hectogram-Scale Synthesis at Low Temperature and Cathodoluminescence.

Tempererature-Controlled Growth Of Zno Nanostructures: Branched Nanobelts And Wide Nanosheets

A Novel Low-Temperature Method to Grow Single-Crystal Zno Nanorods

Optical Properties of Zno Nanowires Grown by Thermal Evaporation

Synthesis of Well-Aligned Zno Nanowires Without Catalysts

Temperature-dependent Photoluminescence of ZnO Nanorods Prepared by a Simple Solution Route

Controllable Synthesis of Highly Dispersed Zno Nanoparticles and Nanorods