Abstract:(Cu47Zr11Ti34Ni8)100−xMox bulk metallic glasses (BMGs) with x=0, 1 and 2at.% and a bulk metallic glass matrix composite with x=5at.% were successfully prepared by water-cooled copper mold casting. The effect of the addition of a small amount of Mo on the glass forming ability (GFA), thermal properties of the base alloy (i.e. x=0) were investigated by X-ray diffraction (XRD), differential scanning calorimetry (DSC) and differential thermal analyzer (DTA). It is found that the addition of appropriate amount of Mo can enhance the GFA of the Cu-based BMG, as indicated by the increase in the reduced glass transition temperature Trg (=Tg/Tl) and the parameter γ (=Tx/(Tg+Tl)) with the increase of Mo. On the other hand, the corrosion resistance of the Cu-based BMGs with different Mo contents was examined by electrochemical polarization and weight loss measurement in 1mol/L H2SO4 and 1mol/L NaOH solutions, respectively. It is found that the corrosion resistance of Cu-based BMGs increased with increasing Mo content with the lowest corrosion rate of (0.9±0.2)×10−3mm/year in 1mol/L H2SO4 solution and (0.3±0.1)×10−3mm/year in 1mol/L NaOH solution, respectively, for the BMG containing 2at.% Mo. X-ray photoelectron spectroscopy (XPS) results revealed that the improvement of corrosion resistance of Cu-based BMG containing appropriate amount of Mo originated from the enrichment of ZrO2 and TiO2, but depletion in Cu- or Ni-oxides in the passive films formed during electrochemical polarization. Finally, the galvanostatic-step measurement was performed to investigate the kinetics of the formation of passive films on the BMG surfaces. It is demonstrated that the addition of an appropriate amount of Mo can effectively improve the stability and uniformity of the passive film. The role of Mo addition on the glass forming ability and corrosion behavior is discussed.

Influence of Cu content on the mechanical properties and corrosion resistance of Mg-Zn-Ca bulk metallic glasses

Effect of Cu on Glass Forming Ability and Mechanical Properties of Mg-Zn-Ca Alloys

Effects of Cu Addition on the Glass Forming Ability and Corrosion Resistance of Ti-Zr-Be-Ni Alloys

Effects of Mg Content and Cooling Rate on Microstructure and Corrosion Behavior of Mg-Cu-Zn-Y Bulk Metallic Glass Composites

Microstructure, Mechanical and Bio-Corrosion Properties of Mn-Doped Mg-Zn-Ca Bulk Metallic Glass Composites

Glass Forming Ability and Corrosion Resistance of Zr-Cu- Ni-Al-Ag Bulk Metallic Glass

Influence of microstructure and chemical compositions on the corrosion properties of Zr-based bulk metallic glasses

Effects of Sr on the glass-forming ability and corrosion behaviour of Mg–Zn–Ca–Cu bulk metallic glass

Effect of Al addition on properties of Cu45Zr45.5Ti9.5 bulk metallic glass

Fe–C micro-alloying effect on properties of Zr53Al11.6Ni11.7Cu23.7 bulk metallic glass

Enhanced Mechanical Properties and Corrosion Resistance of a Mg–Zn–Ca Bulk Metallic Glass Composite by Fe Particle Addition

Effects of Zn Addition on the Improvement of Glass Forming Ability and Plasticity of Mg–Cu–Tb Bulk Metallic Glasses

Composition Design and Properties of Cu–Zr–Ti Bulk Metallic Glass Composites

Corrosion Of, and Cellular Responses to Mg–Zn–Ca Bulk Metallic Glasses

Influence of the Micro-Addition of Mo on Glass Forming Ability and Corrosion Resistance of Cu-based Bulk Metallic Glasses

Ti Microalloying Effect on Corrosion Resistance and Thermal Stability of CuZr-based Bulk Metallic Glasses

Effect of Cu Content and Zn/Mg Ratio on Microstructure and Mechanical Properties of Al–Zn–Mg–Cu Alloys

The effect of microalloying on thermal stability and corrosion resistance of Cu-based bulk metallic glasses

Effects of Ni addition on the glass-forming ability, mechanical properties and corrosion resistance of Zr–Cu–Al bulk metallic glasses

Influence of Ca Addition on Microstructure, Mechanical Properties and Corrosion Behavior of Mg-2Zn Alloy

Formation, Mechanical Properties and Corrosion Behavior of Zr-Al-Co-Er-Cu Bulk Metallic Glasses