Effect of Cu on Glass Forming Ability and Mechanical Properties of Mg-Zn-Ca Alloys

邱克强,王猛,张洪兵,柏笑君,任英磊,张涛

DOI: https://doi.org/10.3321/j.issn:1004-0609.2009.04.013

2009-01-01

The Chinese Journal of Nonferrous Metals

Abstract:Mg70-xZn25Ca5Cux(x=1, 2, 3.5, 5) as-cast alloys with 3 mm in diameter were produced by using copper mold casting method. The microstructures, phase constitutes and mechanical properties of as-cast samples were investigated by scanning electron microscopy (SEM), X-ray diffractometry (XRD) and compression tester. The fracture surfaces were also analyzed by SEM. The results show that the critical sample size for glass formation, the fracture strength and the plastic strain of Mg69Zn25Ca5Cu1 alloy are 3 mm in diameter, 690 MPa and 1.7%, respectively. Both of the glass forming ability and the plastic deformation are improved obviously compared with Mg-Zn-Ca alloys. Up to now the plastic strain is the largest one in the samples with diameter larger than 2 mm for Mg-based bulk metallic glasses.