Transport properties of concrete after drying-wetting regimes to elucidate the effects of moisture content, hysteresis and microcracking
Z. Wu,H.S. Wong,N.R. Buenfeld
DOI: https://doi.org/10.1016/j.cemconres.2017.04.006
IF: 11.958
2017-08-01
Cement and Concrete Research
Abstract:Drying and wetting induce a number of microstructural changes that could impact transport properties and durability of concrete structures, but their significance is not well-established. This research examines pastes, mortars and concretes with different w/b ratios, binders, aggregate sizes, curing and conditioning regimes. 50mm thick samples were dried to equilibrium at either 105°C, 50°C/7% RH, 21°C/33% RH or gentle stepwise at 21°C/93% RH→3% RH, and then rewetted stepwise by humidification at 21°C/33% RH→86% RH and full saturation to produce varying degrees of damage and moisture content. Oxygen diffusivity and permeability, electrical conductivity, microcracking, accessible and total porosity were measured at different conditioning stages over 3-year period to better understand the effects of shrinkage, hysteresis and drying-induced damage on transport properties. The effect of supplementary cementitious materials (GGBS, SF) and implications of drying-wetting on concrete durability are discussed.
construction & building technology,materials science, multidisciplinary