Abstract:Hybrid optical films of TiO2-triethoxysilane-capped polythiourethane (TCPTU) with high refractive indices have been prepared via an in situ sol-gel method. The high refractive index triethoxysilane-capped polythiourethane (TCPTU) was synthesized by polyaddition of the triethoxysilane-modified trimercaptothioethylamine (TMTEA) and 2,2'-dimercaptoethylsulfide (MES) with 2,4-tolylene diisocyanate (TDI). The titania content in the hybrid films can be adjusted from 0 to 80 wt.-% by the feed ratio of titania precursor [Ti(OBu)(4)] to polymer (TCPTU). Both FTIR and DSC analyses indicate that there is chemical bonding between the titania domain and the polymer chain. TGA results suggest that the titania of high content was successfully incorporated into polymer matrices and this series of hybrid films have good thermal properties. AFM measurements indicate that in the hybrid films the titania domains are of nanosize scale and the domain size averagely decrease from 60-80 nm to 5-20 nm with increasing content of titania, and the variation of surface roughness for the hybrid films has the same trend. These may be relative to the content of TCPTU and the interaction between titania and polymer (TCPTU). The refractive indices of the hybrid films at 632.8 nm increased from 1 632 to 1 879 as the titania content varied from 0 to 80 wt.%.

Study on Mechanical, Thermal and Optical Properties of Acrylic Resin/TiO2 Organic-inorganic Hybrid Materials

Study on acrylic resin/titania organic–inorganic hybrid materials prepared by the sol–gel process

PREPARATION OF ACRYLIC RESIN/TiO2 ORGANIC-INORGANIC HYBRID BY SOL-GEL PROCESS AND CHARACTERIZATION OF ITS STRUCTURE

Trialkoxysilane‐capped Acrylic Resin/titania Organic–inorganic Hybrid Optical Films Prepared by the Sol–gel Process

Effect of Preparation of Titania Sol on the Structure and Properties of Acrylic Resin/Titania Hybrid Materials

Sol–gel derived organic–inorganic hybrid from trialkoxysilane-capped acrylic resin and titania: effects of preparation conditions on the structure and properties

Study on in-situ Modification of Vinyl Acetate-Acrylate Latex by Anatase TiO2 Sol

Synthesisi and Characterization of New PMMA-TiO2 Organic-Lnorganic Hybrid Glasses

Poly(Methyl Methacrylate)-Titania Hybrid Materials by Sol-Gel Processing

Synthesis and Characterization of PMMA-ZrO2 (SiO2, TiO2, Al2O3) Organic-Inorganic Hybrid Materials

Preparation and Characterization of Trialkoxysilane‐Containing Acrylic Resin/Alumina Hybrid Materials

Microstructure and Properties of Polyester-Based Polyurethane/titania Hybrid Films Prepared by Sol–gel Process

Study on Acrylic Resin/Alumina Hybrid Materials Prepared by the Sol‐Gel Process

Trialkoxysilane‐capped Acrylic Resin/alumina Hybrid Materials Prepared by in Situ Sol–gel Process

Preparation and Properties of Thermosetting Acrylic Coatings Using Titanium-Oxo-Cluster As A Curing Agent

Synthesis and Characterization of PMMA-ZrO<sub>2</sub>(SiO<sub>2</sub>,TiO<sub>2</sub>,Al<sub>2</sub>O<sub>3</sub>) Organic-Inorganic Hybrid Materials

Preparation and Characterization of Acrylic/Nano-Tio2 Composite Latex

Acrylic‐Based Polyurethane/Silica Hybrids Prepared by Acid‐Catalyzed Sol–Gel Process: Structure and Mechanical Properties

Thermal Properties of Novel 9,10-Dihydro-9-oxa-10-phosphaphenanthrene 10-Oxide-based Organic/Inorganic Hybrid Materials Prepared by Sol–Gel and UV-Curing Processes

Mechanical Properties of Interface‐free Polyacrylate‐silica Hybrid Sol–gel Materials for Potential Dental Applications

Research On Preparation, Structure And Properties Of Tio2/Polythiourethane Hybrid Optical Films With High Refractive Index