MICROSTRUCTURES AND HYDROGEN STORAGE PROPERTIES OF Ti0.7Zr0.3(Cr1-xVx)2 ALLOYS

Ma Ping,Wu Erdong,Li Wuhui,Sun Kai,Chen Dongfeng

DOI: https://doi.org/10.3724/sp.j.1037.2013.00637

IF: 1.797

2014-01-01

ACTA METALLURGICA SINICA

Abstract:The crystal structures and phase compositions of Ti0.7Zr0.(3)(Cr1-xVx)(2) (x=0.1, 0.2, 0.3, 0.4) alloys are analyzed by the XRD and SEM. The hydrogen storage properties, activation performance, thermodynamics and high-temperature desorption process of the alloys are investigated by pressure-composition-temperature (P-C-T) and DTA-TG measurements. The results show that the Ti-0.7,Zr-0.3(Cr1-xVx)(2) alloys contain multi-phases, i.e. C36 (P6(3)/mmc) and C15 (Fd3m) Laves phases and V-based bcc solid solution phases with different lattice constants. When the content of V in the alloy is low, the alloy basically consists Of C36 type of Laves phase and small amount of bcc solid solution phase. As the content of V increases, the C36 type transfers into C15 type of Laves phase, where the probability of forming third type of stacking layers (C layers) increases, and the content of the bcc solid solution also increases. The alloys in bulk can be easily activated at 2 MPa and room temperature. The x=0.1, 0.2 alloys present excellent activation performance even after exposure in air for 20 d. As V content increases, the hydrogen absorption capacity of the alloy increases whereas the plateau pressure decreases. The relative partial molar enthalpy (Delta E) and entropy (Delta S) of hydrogen absorption for the alloys are found to be in the ranges of-7 similar to-28 kJ/mol and 35 95 J/(mol center dot K). The DTA-TG analysis indicates that the hydrogen release from the hydrides of the alloys occur in two dissolving temperatures within the range of 500 similar to 600 K, and some residual hydrides have completely decomposed at heating temperature up to 800 K.