Abstract:This study emphasizes and the testing of alumina particles via a fabricated planetary ball mill. The fabrication of planetary ball mill work began with the design of the machine. Parts were fabricated separately then assembled. The jar and grinding media were made up of stainless steel as it as a higher strength property than Alumina powder. Testing and calibration are carried out through the response surface methodology utilizing the experimental results. Test is also executed to confirm the validity and the accuracy of the developed planetary ball mill. Based on the result obtain, the alumina powders have a particle size reduction of about 50% of the original particle size. Furthermore, the shape of the alumina particle changes from angular to irregular particle shape. It is apparent that the fabricated planetary ball mill able to grind the alumina powders and produce ultrafine particles by given period and parameter set. The fabricated ball mill able to function better than conventional ball mill. The planetary ball mill will be useful for the laboratory use purpose and production of ultrafine powder production. This ultrafine powder production can be used in application of powder metallurgy and advanced material research purposes.

Fabrication of Sn Coatings on Alumina Balls by Mechanical Coating Technique and Relevant Process Analysis

Fabrication of Zinc Coatings on Alumina Balls from Zinc Powder by Mechanical Coating Technique and the Process Analysis

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

Formation Process of Ti Coatings in Mechanical Coating with Different Rotation Speed

The influence of the processing parameters on the formation of iron thin films on alumina balls by mechanical coating technique

In Situ Formation of Al2O3–SiO2–SnO2 Composite Ceramic Coating by Microarc Oxidation on Al–20%Sn Alloy

Influence of Metal Properties on the Formation and Evolution of Metal Coatings During Mechanical Coating

Preparation of Metal Coatings on Steel Balls Using Mechanical Coating Technique and Its Process Analysis

Effect of deposition parameter on properties of AlSn20Cu coating prepared by magnetron sputtering

Deposition of NiAl/Al3Ni2(CrB2) Coatings from Ni, Al and CrB2 Powders Using Mechanical Synthesis in Planetary Ball Mill

S0430204 Formation and Its Process Analysis of Metal Films by Mechanical Coating Technique

The influence of process parameters on the formation of Al coating on steel by planetary ball-milling

Synthesis of Nano-phase Composite Al-Sn Alloy by Reaction Ball Milling Process and Its Performance

Simple Synthesis of the Composite Coating and the Lubrication Mechanisms of the Spherical SnAgCu–Al2O3

Production and Characterization of Nanocrystalline SnO2 Films on Al2O3 Agglomerates by CVD in a Fluidized Bed

Morphology and structure analyses of SnO 2 thin film coated on Al 2 O 3 ultrafine particles by gas phase reaction in fluidized bed

Synthesis and Characterization of a Self-Lubricating Film on Bearing Balls

Surface patterning of ZrO2 ceramicsnum using Sn-Al Alloy at a low temperature

Analysis Of Alumina Particles Size And Shape Formation From Developed Planetary Ball Mill

Mechanical Coating Technique and Its Development As a Novel Film Formation Process

Microstructure and Wear Properties of Al-Based Bearing Alloys Fabricated by Mechanical Alloying