Improved Ionic Conductivity and Air Stability of Li7P3S11 by SnSe2 Doping and Two-Step Pressing Sintering Method
Yuhua Zhen,Wenjie Yang,Zheng Qin,Mengxin Ji,Yuanyue Qie,Jiahao Li,Gaohui Ren,Qingzhong Xue,Yuhua Chi,Wei Xing,Hongxia Geng
DOI: https://doi.org/10.1016/j.electacta.2024.144888
IF: 6.6
2024-01-01
Electrochimica Acta
Abstract:The ideal solid-state electrolyte must possess high ionic conductivity and exceptional chemical and electrochemical stability. We prepared 70Li(2)S-(30 - x)P2S5-xSnSe(2) (x = 0, 0.5, 1, 1.5, 2, 3) glass-ceramic electrolytes doped with SnSe2 using a facile high-energy ball milling combined with an annealing process. We utilized a "two-step pressing method" to eliminate defects such as voids generated during annealing. Through the use of X-ray powder diffraction (XRD) and energy-dispersive spectroscopy (EDS) mappings, we confirmed that a small amount of SnSe2 can be successfully and uniformly doped into the framework of the solid-state electrolyte. In particular, the 70Li(2)S-28.5P(2)S(5)-1.5SnSe(2) (Li7P2.85Sn0.075S10.625Se0.15) glass-ceramic exhibits the highest conductivity of 2.62 x 10(-3) S center dot cm(-1) at room temperature, along with excellent electronic insulation and a stable -0.5 to 5 V (vs. Li/Li+) high-voltage platform. Furthermore, our combination of various methods, such as the LCR digital electric bridge, has proven that the doping of SnSe2 effectively enhances the chemical stability. Moreover, all-solid-state batteries assembled based on Li7P2.85Sn0.075S10.625Se0.15 electrolyte demonstrate enhanced rate capability and cycling stability. These results indicate that the Li7P2.85Sn0.075S10.625Se0.15 electrolyte can effectively construct high-performance all-solid-state batteries, facilitating industrial production and widespread adoption.