Abstract:Here the discovery of mixed OH−/H+ conduction in doped SrCeO3 ceramics at temperatures below 100 °C is presented. A typical high ionic conductivity of 20% Y doped SrCeO3 in water is 12 mS cm−1 at 60 °C. Ionic conductivity of oxides in KOH solution is greatly enhanced due to 'feeding effect'. The drawbacks of high temperature solid oxide fuel cells (HT‐SOFCs) prompt efforts to lower operating temperatures to near ambient temperatures (NAT). Here the high mixed OH−/H+ ionic conductivity in doped SrCeO3 below 100 °C is reported. The SrCe0.8Y0.2O3−δ (SCYO20) electrolyte demonstrates a high ionic conductivity of 12 mS cm−1 in water and 9 mS cm−1 in wet air at 60 °C and an excellent long‐term stability over 100 h. Solid state nuclear magnetic resonance confirms the presence of protons and hydroxide ions in the hydrated oxides and their correlation with Y dopant. Demonstration of direct ammonia fuel cells using the SCYO20 electrolyte indicates the practical application value of this material. The OH− conduction of SrCe0.7Sn0.2Y0.1O3−δ (SCSY721) is demonstrated by electrolysis of D2O. The introduction of KOH significantly increases the availability of OH− feed ions, leading to a remarkable improvement of ionic conductivity of SCSY721 electrolyte which is increased by 27 times, 56.34 mS cm−1 in 6 m KOH at 90 °C. The increased ionic conductivity due to the presence of high concentration of extrinsic conducting ions, here are OH− ions, is called as 'feeding effect'. This study offers new electrolyte materials for cost‐effective, and durable electrochemical devices such as NAT‐SOFCs.

Intermediate Temperature Electrical Properties in 4 Mol% ZnO-doped Zr0.92Y0.08O2-α/NaCl-KCl Composite Electrolyte

Yb2o3 Doped Zr0.92y0.08o2-(8ysz) And Its Composite Electrolyte For Intermediate Temperature Solid Oxide Fuel Cells

A Novel MgO Doped Zr0.92Y0.08O2-α(8YSZ) with NaCl/KCl Composite Electrolyte for Intermediate Temperature Fuel Cells

Novel Composite Electrolytes Of Zr0.92y0.08o2-Alpha(8ysz)-Low Melting Point Glass Powder For Intermediate Temperature Solid Oxide Fuel Cells

Synthesis and Intermediate Temperature Electrical Properties of Zr0.84Y0.12Nd0.04O2-α-Low Melting Point Glass Powder Composite Electrolyte

High-performance Intermediate Temperature Fuel Cells of New SrCe 0.9 Yb 0.1 O 3−α -Inorganic Salt Composite Electrolytes

Enhanced Electrochemical Properties of Lu-doped BaCeO3 and KCl-NaCl Composite As Electrolyte for Intermediate Temperature Solid Oxide Fuel Cells

Novel SrCe1 − Xybxo3 − Α-(Na/k)cl Composite Electrolytes for Intermediate Temperature Solid Oxide Fuel Cells

Synthesis and Intermediate Temperature Electrical Properties of SrCe0.9 Yb0.1 O3-α-LiCl-KCl Composite Electrolyte

BaCe0.9Er1.1O3-α-NaCl-KCl Composite As Electrolyte for Intermediate Temperature Solid Oxide Fuel Cells

ZnO-doped BaZr0.85Y0.15O3−δ proton-conducting electrolytes: Characterization and fabrication of thin films

BaZr0.8Y0.2O3−δ electrolyte with and without ZnO sintering aid: Preparation and characterization

Study on the Properties of Ysz Electrolyte Made by Plaster Casting Method and the Applications in Solid Oxide Fuel Cells

Low Temperature Synthesis of Novel SrCe0.9Yb0.1O3−α-chlorides Composite Electrolytes for Intermediate Temperature Protonic Ceramics Fuel Cells

Ionic Conductivity of Electrolytes Composed of Oleate-Capped Yttria-Stabilized Zirconia Nanoparticles

Effect of Two Different ZnO Addition Strategies on the Sinterability and Conductivity of the BaZr0.4Ce0.4Y0.2O3−δ Proton-Conducting Ceramic Electrolyte

Low Temperature Fast Mixed OH−/H+ Ionic Conductor in Doped Strontium Cerates

Low Temperature Synthesize SrCe0.85Er0.15O3－α Using Sol-Gel Method and Its Composite Electrolyte for Intermediate Temperature Fuel Cell

Intermediate Temperature Fuel Cell Durability of Eu-doped SrCeO3-SrZrO3 Solid Solution/ NaCl-KCl Composite Electrolyte

High-conductivity electrolyte with a low sintering temperature for solid oxide fuel cells

Effects of ZnO Sintering Additive on the Sintering Behavior and Conductivity of YSZ Solid Electrolyte