Abstract:SrCeO3 and SrCe0.9Sm0.1O3-α were synthesized using a high-temperature solid-state reaction method using Sm2O3, SrCO3, CeO2 as precursors, then the SrCe0.9Sm0.1O3-α-NaCl-KCl composite electrolyte was fabricated by compounding SrCe0.9Sm0.1O3-α with NaCl-KCl and sintering it at a lower temperature (750 °C) than that of a single SrCeO3 material (1540 °C). The phase and microstructure of the samples were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The conductivities of the samples were measured in dry nitrogen atmosphere using electrochemical analyzer. The conductivities of the SrCeO3, SrCe0.9Sm0.1O3-α and SrCe0.9Sm0.1O3-α-NaCl-KCl at 700 °C were 2.09 × 10−5 S·cm−1, 1.82 × 10−3 S·cm−1 and 1.43 × 10−1 S·cm−1 respectively. The conductivities of SrCe0.9Sm0.1O3-α-NaCl-KCl composite electrolyte are four orders of magnitude higher than those of SrCeO3 and two orders of magnitude higher than those of SrCe0.9Sm0.1O3-α. The result of logσ ~ logpO2 plot indicates that SrCe0.9Sm0.1O3-α-NaCl-KCl is almost a pure ionic conductor. The electrolyte resistance and the polarization resistance of the H2/O2 fuel cell based on SrCe0.9Sm0.1O3-α-NaCl-KCl composite electrolyte under open-circuit condition were 1.0 Ω·cm2 and 0.2 Ω·cm2 respectively. Further, the obtained maximum power density at 700 °C was 182 mW·cm−2.

Novel SrCe1 − Xybxo3 − Α-(Na/k)cl Composite Electrolytes for Intermediate Temperature Solid Oxide Fuel Cells

A stable and easily sintering BaCeO3-based proton-conductive electrolyte

Low Temperature Synthesis of Novel SrCe0.9Yb0.1O3−α-chlorides Composite Electrolytes for Intermediate Temperature Protonic Ceramics Fuel Cells

High-performance Intermediate Temperature Fuel Cells of New SrCe 0.9 Yb 0.1 O 3−α -Inorganic Salt Composite Electrolytes

Intermediate Temperature Electrochemical Properties of Yb3+ Doped SrCeO3- Carbonate and Chloride Composite Electrolytes

Enhanced Electrochemical Properties of Lu-doped BaCeO3 and KCl-NaCl Composite As Electrolyte for Intermediate Temperature Solid Oxide Fuel Cells

BaCe0.9Er1.1O3-α-NaCl-KCl Composite As Electrolyte for Intermediate Temperature Solid Oxide Fuel Cells

SrCe0.9Sm0.1O3-α Compounded with NaCl-KCl As a Composite Electrolyte for Intermediate Temperature Fuel Cell

Low Temperature Synthesize SrCe0.85Er0.15O3－α Using Sol-Gel Method and Its Composite Electrolyte for Intermediate Temperature Fuel Cell

Synthesis and Intermediate Temperature Electrical Properties of SrCe0.9 Yb0.1 O3-α-LiCl-KCl Composite Electrolyte

Synthesis and Conductivity of Strontium Cerate Doped by Erbium Oxide and Its Composite Electrolyte for Intermediate Temperature Fuel Cell

Low Temperature Synthesis of SrCe0.9Eu0.1O3-α by Sol-Gel Method and SrCe0.9Eu0.1O3-α-NaCl-KCl Composite Electrolyte for Intermediate Temperature Fuel Cells

Yb2o3 Doped Zr0.92y0.08o2-(8ysz) And Its Composite Electrolyte For Intermediate Temperature Solid Oxide Fuel Cells

Intermediate Temperature Fuel Cell Durability of Eu-doped SrCeO3-SrZrO3 Solid Solution/ NaCl-KCl Composite Electrolyte

A Novel Gd3+ and Yb3+ Co-Doped Ceria-Sulphate Composite Electrolyte for Intermediate-Temperature Fuel Cells

High Performance Gd3+ and Y3+ Co-Doped Ceria-Based Electrolytes for Intermediate Temperature Solid Oxide Fuel Cells

Preparation and electrochemical characterization of Er3+-doped ceria-chloride composite electrolyte for intermediate-temperature solid oxide fuel cells

Intermediate Temperature Electrochemical Properties of Lutetium-Doped SrCeO3/SrZrO3-molten Carbonate Composite Electrolyte

Cobalt-free Sr0.7Y0.3CuO2+δ As a Cathode for Intermediate-Temperature Solid Oxide Fuel Cell

Synthesis And Characterization Of Bazr0.3ce0.5y0.2-Xybxo3-Delta Proton Conductor For Solid Oxide Fuel Cells

Sr-Yb Co-doping of BaCe0.4Zr0.6O3 Proton-Conducting Electrolyte for Solid Oxide Fuel Cells