Abstract:A newly developed method for the formation of nanowires by self-aggregation of nanoparticles is presented in this paper. Co3C, Co-rich, and Ni nanoparticles dispersed on holey carbon grids are inserted in a vacuum oven and are co-annealed with PolyChloroTriFluoroEthylene (PCTFE) at 375 degrees C. No external electric or magnetic fields were applied. High resolution electron microscopy (HREM) was extensively used to determine the shape, size distribution and crystallographic phase of the starting and produced materials. Interestingly, after an annealing circle of 72 hours, the nanoparticles seem to self-agglomerate into nanowires which have diameters in the 5-20 nm range and lengths exceeding at cases 1 micron. The diameter of the produced wires is in the same range as the diameter of the initial nanoparticles, further supporting the notion that the nanowires have formed out of nanoparticle agglomeration. Close inspection of nanowire HREM images shows that the core structure of nanowires wider than approximately 11 nm resembles linked nanoparticles. Phase identification performed using the HREM images reveals the core is of the same phase/material as the starting nanoparticles. Since nanowires appear to form over holes on the holey carbon grid, a base growth mechanism is proposed. The fluorocarbon vapour decomposes over the transitional metal nanoparticles and carbon tubules start growing. The nanoparticles appear to be trapped inside the tubules where their close proximity enhances their fusion into a continuous core. At the studied temperature, the nanoparticle fusion is seen to be limited by the size of the nanoparticles manifested by continuous cores only in the thin nanowires. The process presented here shows that nanoparticles can spontaneously self-align into nanowires in a way and to an extent never reported before. Therefore there is certainly scope for studying this method further to reveal more information about the catalytic action of transitional metals on hydrocarbons and the exact nanowire formation mechanism. Although it is currently a matter of speculation, this process might lead to the effortless growth of nanowires at particular places when building miniature circuits.

Self-Assembly Mechanism of Ni Nanowires Prepared with an External Magnetic Field

Spontaneous self-agglomeration of magnetic nanoparticles into nanowires

Size- and Structure-Controlled Synthesis and Characterization of Nickel Nanoparticles

Solution-phase synthesis of nickel phosphide single-crystalline nanowires

Room temperature synthesis and one-dimensional self-assembly of interlaced Ni nanodiscs under magnetic field

Template-Free Synthesis and Self-Assembly of Aligned Nickel Nanochains under Magnetic Fields

Magnetic nanochains of metal formed by assembly of small nanoparticles.

Experimental and Micromagnetics Studies on Magnetism of Ni Nanowire Arrays Prepared with Magnetic Field Induction

Thermodynamic Phase Formation of Morphology and Size Controlled Ni Nanochains by Temperature and Magnetic Field

Fabrication of One-Dimensional Magnetic Particles Chain of Polycrystalline Nickel under Magnetic Field

Electrochemical fabrication and structure of Ni<sub><i>x</i></sub>Zn<sub>1−<i>x</i></sub> alloy nanowires

Nickel Chains Assembled by Hollow Microspheres and Their Magnetic Properties

Synthesis of Cobalt Nanowires by Template-Free Method

Facile and rapid synthesis of nickel nanowires and their magnetic properties

Magnetic field-induced solvothermal synthesis of one-dimensional assemblies of Ni-Co alloy microstructures

CTAB-mediated synthesis of iron–nickel alloy nanochains and their magnetic properties

Fabrication and Magnetism of Radial-easy-magnetized Ni Nanowire Arrays

Magnetic behaviour of arrays of nickel nanowires with small diameter

Magnetic-Field-Induced Formation Of One-Dimensional Magnetite Nanochains

Diameter-Controlled Synthesis of Polycrystalline Nickel Nanowires and Their Size Dependent Magnetic Properties

A Self-Assembly of Single Layer of Co Nanorods to Reveal the Magnetostatic Interaction Mechanism