Magnetic behaviour of arrays of nickel nanowires with small diameter

Kuan-Hong Xue,Gu-Ping Pan,Ming-Hu Pan,Mu Lu,Guang-Hou Wang

DOI: https://doi.org/10.1016/S0749-6036(03)00051-X

IF: 3.22

2003-01-01

Superlattices and Microstructures

Abstract:Arrays of nickel nanowires have been fabricated within a template of porous alumina by electrochemical deposition. Measurements of magnetic hysteresis loops were performed at room temperature with a vibrating sample magnetometer. Coercivity and squareness of the arrays are closely related to l/D and diameter of the nanowires, and the angle θ between the normal line of the alumina surface and the applied magnetic field. For the same diameter of 10 nm, the coercivity and squareness increase remarkably with l/D when the l/D is less than 100. The diameter and angle θ dependences of coercivity do not follow the relationships of curling, fanning or coherent rotation mode of magnetization while thermal activation for magnetization reversal becomes remarkable for the arrays of Ni nanowires with the diameter less than 18 nm but the same l/D of 50. The coercivity of the arrays with the magnetic field perpendicular to the film surface is linear with D−3/2 of Ni nanowires. From the fitting line, the critical diameter for superparamagnetism at room temperature and pure coercivity for such Ni nanowire arrays are found to be 6 nm and 1200 Oe respectively.