Abstract:Magnetic properties with 3 different sizes of Ni nanochains, synthesized by a technique of wet chemical solution, have been investigated experimentally. The sample sizes are 50 nm, 75 nm, and 150 nm with a typical length of a few microns. The characterizations by XRD and TEM reveal that the samples consist of Ni nano-particles forming one dimensional (1D) chain-like structure. The magnetic properties have been investigated by FC, ZFC measurements and M-H measurements. The results can be well explained within the context of core-shell model. First of all, the freezing of disordered spins in the shell layer have resulted in a peak-like structure on the ZFC curve. The peak position occurs around TF 13 K. With the 50 nm sample, the field dependent behavior of TF(H) has been investigated in detail. It is well described by the de Almeida-Thouless (AT) equation for the surface spin glass state. Secondly, the shape anisotropy of 1D structure has caused a wide separation between the FC and ZFC curves. This is mainly attributed to the blocking of the core magnetism. Thirdly, by the M-H measurement in the low field region, the open hysteresis loop measured at 5 K < TF is significantly enlarged in comparison with that taken at T > TF. This indicates that a significant part of the contribution to the magnetic irreversibility at T < TF is coming from the disordered spins in the shell layer. Lastly, with reducing sample size, the coercivity, HC, increases, whereas the saturation magnetization goes down dramatically. These imply that, as the sample size reduces, the effect of shape anisotropy becomes larger in the magnetization reversal process and the contribution to the magnetism from the ferromagnetically ordered core becomes smaller.

Size-dependent Magnetic Properties of Nickel Nano-Chains

Size-dependent Magnetic Properties of Branchlike Nickel Oxide Nanocrystals

Magnetization Reversal and Anisotropy with Chains of Superparamagnetic Ni Nanoparticles.

Size Dependence of the Magnetic Properties of Ni Nanoparticles Prepared by Thermal Decomposition Method

Thermodynamic Phase Formation of Morphology and Size Controlled Ni Nanochains by Temperature and Magnetic Field

Size- and Structure-Controlled Synthesis and Characterization of Nickel Nanoparticles

Synthesis of Ni Nanochains with Various Sizes: the Magnetic and Catalytic Properties

Magnetic-Properties of Ultrafine Nickel Particles

Partial Cationic Inversion-Induced Magnetic Hardening of Densely Packed 23-Nm-sized Nanocrystallite-Interacting Nickel Ferrite Electrospun Nanowires

Size-dependent saturation magnetization and Curie temperature of nanocrystalline nickel

Ni/Ni3C Core-Shell Nanochains and Its Magnetic Properties: One-Step Synthesis at low temperature

Magnetic nanochains of metal formed by assembly of small nanoparticles.

Magnetic behaviour of arrays of nickel nanowires with small diameter

Synthesis and magnetic properties of nickel nanocrystals

Diameter-Controlled Synthesis of Polycrystalline Nickel Nanowires and Their Size Dependent Magnetic Properties

Selective Synthesis of Peapodlike Ni/Ni3S2 Nanochains and Nickel Sulfide Hollow Chains and Their Magnetic Properties

Surface magnetic states of Ni nanochains modified by using different organic surfactants

Size-Dependent Curie Transition of Ni Nanocrystals

Structure, Magnetic and Magnetocaloric Properties of Ni2MnGa Heusler Alloy Nanowires

CTAB-mediated synthesis of iron–nickel alloy nanochains and their magnetic properties

Weak ferromagnetism and spin glass state with nano-sized nickel carbide