Abstract:A newly developed method for the formation of nanowires by self-aggregation of nanoparticles is presented in this paper. Co3C, Co-rich, and Ni nanoparticles dispersed on holey carbon grids are inserted in a vacuum oven and are co-annealed with PolyChloroTriFluoroEthylene (PCTFE) at 375 degrees C. No external electric or magnetic fields were applied. High resolution electron microscopy (HREM) was extensively used to determine the shape, size distribution and crystallographic phase of the starting and produced materials. Interestingly, after an annealing circle of 72 hours, the nanoparticles seem to self-agglomerate into nanowires which have diameters in the 5-20 nm range and lengths exceeding at cases 1 micron. The diameter of the produced wires is in the same range as the diameter of the initial nanoparticles, further supporting the notion that the nanowires have formed out of nanoparticle agglomeration. Close inspection of nanowire HREM images shows that the core structure of nanowires wider than approximately 11 nm resembles linked nanoparticles. Phase identification performed using the HREM images reveals the core is of the same phase/material as the starting nanoparticles. Since nanowires appear to form over holes on the holey carbon grid, a base growth mechanism is proposed. The fluorocarbon vapour decomposes over the transitional metal nanoparticles and carbon tubules start growing. The nanoparticles appear to be trapped inside the tubules where their close proximity enhances their fusion into a continuous core. At the studied temperature, the nanoparticle fusion is seen to be limited by the size of the nanoparticles manifested by continuous cores only in the thin nanowires. The process presented here shows that nanoparticles can spontaneously self-align into nanowires in a way and to an extent never reported before. Therefore there is certainly scope for studying this method further to reveal more information about the catalytic action of transitional metals on hydrocarbons and the exact nanowire formation mechanism. Although it is currently a matter of speculation, this process might lead to the effortless growth of nanowires at particular places when building miniature circuits.

Diameter-Controlled Synthesis of Polycrystalline Nickel Nanowires and Their Size Dependent Magnetic Properties

Size- and Structure-Controlled Synthesis and Characterization of Nickel Nanoparticles

Controlled one-step synthesis of spiky polycrystalline nickel nanowires with enhanced magnetic properties

Facile and rapid synthesis of nickel nanowires and their magnetic properties

Size-dependent Magnetic Properties of Branchlike Nickel Oxide Nanocrystals

Controlled Synthesis of Hierarchical Nickel and Morphology-Dependent Electromagnetic Properties

On the Growth Mechanism of Nickel and Cobalt Nanowires and Comparison of Their Magnetic Properties

Magnetic Field Effects on the Formation and Properties of Nickel Nanostructures

Controlled Synthesis and Magnetic Properties of Ni Nanotubes and Nanowires

Large magnetic anisotropy enhancement in size controlled Ni nanowires electrodeposited into nanoporous alumina templates

Spontaneous self-agglomeration of magnetic nanoparticles into nanowires

Controlled Synthesis and Characterizations of Ni Nanoscale Crystals by Microwave-Assisted Polyol Method

Preparation of hexagonal close-packed nickel nanoparticles via a thermal decomposition approach using nickel acetate tetrahydrate as a precursor

Preparation and physical properties of soft magnetic nickel-cobalt nanowires with modulated diameters

Synthesis of Nickel Nanowires (Ni-Nws) As High Ferromagnetic Material by Electrodeposition Technique

Magnetic behaviour of arrays of nickel nanowires with small diameter

Experimental and Micromagnetics Studies on Magnetism of Ni Nanowire Arrays Prepared with Magnetic Field Induction

Synthesis of Ni Nanochains with Various Sizes: the Magnetic and Catalytic Properties

Size-dependent magnetic properties of nickel nanochains

Controlled Synthesis of 3d and 1d Nickel Nanostructures Using an External Magnetic Field Assisted Solution-Phase Approach

Magnetic-Properties of Ultrafine Nickel Particles