Abstract:Magnetic properties with 3 different sizes of Ni nanochains, synthesized by a technique of wet chemical solution, have been investigated experimentally. The sample sizes are 50 nm, 75 nm, and 150 nm with a typical length of a few microns. The characterizations by XRD and TEM reveal that the samples consist of Ni nano-particles forming one dimensional (1D) chain-like structure. The magnetic properties have been investigated by FC, ZFC measurements and M-H measurements. The results can be well explained within the context of core-shell model. First of all, the freezing of disordered spins in the shell layer have resulted in a peak-like structure on the ZFC curve. The peak position occurs around TF 13 K. With the 50 nm sample, the field dependent behavior of TF(H) has been investigated in detail. It is well described by the de Almeida-Thouless (AT) equation for the surface spin glass state. Secondly, the shape anisotropy of 1D structure has caused a wide separation between the FC and ZFC curves. This is mainly attributed to the blocking of the core magnetism. Thirdly, by the M-H measurement in the low field region, the open hysteresis loop measured at 5 K < TF is significantly enlarged in comparison with that taken at T > TF. This indicates that a significant part of the contribution to the magnetic irreversibility at T < TF is coming from the disordered spins in the shell layer. Lastly, with reducing sample size, the coercivity, HC, increases, whereas the saturation magnetization goes down dramatically. These imply that, as the sample size reduces, the effect of shape anisotropy becomes larger in the magnetization reversal process and the contribution to the magnetism from the ferromagnetically ordered core becomes smaller.

Template-Free Synthesis and Self-Assembly of Aligned Nickel Nanochains under Magnetic Fields

Room temperature synthesis and one-dimensional self-assembly of interlaced Ni nanodiscs under magnetic field

Thermodynamic Phase Formation of Morphology and Size Controlled Ni Nanochains by Temperature and Magnetic Field

Template-Free Synthesis of Magnetic Chains Self-Assembled from Urchin-Like Hierarchical Ni Nanostructures

Size- and Structure-Controlled Synthesis and Characterization of Nickel Nanoparticles

CTAB-mediated synthesis of iron–nickel alloy nanochains and their magnetic properties

Fabrication of One-Dimensional Magnetic Particles Chain of Polycrystalline Nickel under Magnetic Field

(110) Orientation growth of magnetic metal nanowires with face-centered cubic structure using template synthesis technique

Magnetic nanochains of metal formed by assembly of small nanoparticles.

Nickel Chains Assembled by Hollow Microspheres and Their Magnetic Properties

Synthesis of Cobalt Nanowires by Template-Free Method

Ni/Ni3C Core-Shell Nanochains and Its Magnetic Properties: One-Step Synthesis at low temperature

Size-dependent Magnetic Properties of Nickel Nano-Chains

Selective Synthesis of Peapodlike Ni/Ni3S2 Nanochains and Nickel Sulfide Hollow Chains and Their Magnetic Properties

Well-Aligned Copt Hollow Nanochains Synthesized in Water at Room Temperature

Magnetic field-induced solvothermal synthesis of one-dimensional assemblies of Ni-Co alloy microstructures

Template-Based Synthesis and Magnetic Properties of Mn-Zn Ferrite Nanotube and Nanowire Arrays

Template assisted self-assembly of individual and clusters of magnetic nanoparticles

Synthesis of Ni Nanochains with Various Sizes: the Magnetic and Catalytic Properties

Controlled Synthesis and Magnetic Properties of Ni Nanotubes and Nanowires

Simple Electroless Synthesis of Cobalt Nanoparticle Chains, Oriented by Externally Applied Magnetic Fields