Abstract:The effect of extrusion on the microstructure, mechanical property, corrosion behavior, and in vitro biocompatibility of as-cast Mg-1.5Zn-1.2Y-0.1Sr (wt.%) alloy was investigated via tensile tests, electrochemical methods, immersion tests, methylthiazolyl diphenyltetrazolium bromide (MTT), and analytical techniques. Results showed that the as-cast and as-extruded Mg-1.5Zn-1.2Y-0.1Sr alloys comprised an α-Mg matrix and Mg3Y2Zn3 phase (W-phase). In the as-cast alloy, the W-phase was mainly distributed at the grain boundaries, with a small amount of W-phase in the grains. After hot extrusion, the W-phase was broken down into small particles that were dispersed in the alloy, and the grains were refined considerably. The as-extruded alloy exhibited appropriate mechanical properties that were attributed to refinement strengthening, dispersion strengthening, dislocation strengthening, and precipitation strengthening. The as-cast and as-extruded alloys exhibited galvanic corrosion between the W-phase and α-Mg matrix as the main corrosion mechanism. The coarse W-phase directly caused the poor corrosion resistance of the as-cast alloy. The as-extruded alloy obtained via hydrogen evolution and mass loss had corrosion rates of less than 0.5 mm/year. MTT, high-content screening (HCS) analysis, and cell adhesion tests revealed that the as-extruded alloy can improve L929 cell viability and has great potential in the field of biomedical biodegradable implant materials.

Relationship Between Extrusion, Y and Corrosion Behavior of Mg–Y Alloy in NaCl Aqueous Solution

Effect of Microstructure on the Corrosion Behavior of as-cast and Extruded Mg–Sn–Y Alloys

Improvement of Mechanical Properties and Corrosion Resistance of As‐Extruded Mg–2Zn–2Al–0.3Mn Alloy Through Y Addition

Comparative Study on Corrosion Behavior of As-Cast and Extruded Mg–5Y–7Gd–1Nd–0.5Zr Alloy in 5% NaCl Aqueous Solution

Effect of grain size and crystal orientation on the corrosion behavior of as-extruded Mg-6Gd-2Y-0.2Zr alloy

Comparative Study on Corrosion Behavior and Mechanism of As-Cast Mg–Zn–Y and Mg–Zn–Gd Alloys

Corrosion Behavior of Mg-Zn-Y-Zr Alloys in Nacl Solution

Effect of Solid-Solution Treatment on Corrosion and Electrochemical Behaviors of Mg-15Y Alloy in 3.5 Wt.% NaCl Solution

Influence of Rare Earth Element (Y) on Microstructure and Corrosion Behavior of Hot Extrusion AZ91 Magnesium Alloy

Effect of CaCl2 and NaHCO3 in Physiological Saline Solution on the Corrosion Behavior of an As-Extruded Mg–Zn–Y–Nd alloy

Effects of Y on Microstructure and Mechanical Properties of Extruded Mg-5Al-1Ca Magnesium Alloys

Corrosion behavior and mechanical properties of extruded low-alloyed Mg−0.5Bi−0.5Y−0.2Zn alloy

Comparison of the Corrosion Behaviors of Mg–Gd–Y–Zn–Zr Alloys Fabricated by Different Preparation Methods

Effect of Extrusion on Mechanical Property, Corrosion Behavior, and In Vitro Biocompatibility of the As-Cast Mg-Zn-Y-Sr Alloy

Effect of extrusion process on microstructure and mechanical and corrosion properties of biodegradable Mg−5Zn−1.5Y magnesium alloy

Effect of Y Contents on the Microstructure, Mechanical Properties, and Corrosion Behavior of Biomedical Mg‐0.5Zn Alloy

Investigation on corrosion behavior and mechanical properties of an extruded Mg-Zn-Al-Sn-Mn alloy

Structure, mechanical and corrosion properties of extruded Mg-Nd-Zn, Mg-Y-Zn and Mg-Y-Nd alloys

Roles of micro-alloyed Y and Gd in improving the corrosion resistance and mechanical properties of pure Mg

Effects of extrusion parameters on the microstructure, corrosion resistance, and mechanical properties of biodegradable Mg–Zn–Gd–Y–Zr alloy

Investigation of Corrosion Behaviors of Mg–6Gd–3Y–0.4Zr Alloy in NaCl Aqueous Solutions