Abstract:The continuous exploitation of zinc blend resources leads to primary resources may not be sufficient for future requirements. The abundant low-grade lead–zinc oxysulphide ore will become a crucial source of zinc metal. Thus, methods for utilising low-grade lead–zinc ore resources must be urgently developed; this can contribute to achieving considerable economic value. By studying the mineral technology and thermodynamics of low-grade lead–zinc oxysulphide ore, a Box–Behnken design model of response surface methodology was created to explore the impact of various factors, such as reduction time, temperature, and carbon mass ratio. The outcomes of the study indicate that the aforementioned factors have a significant impact on the zinc volatilisation rate, and it reaches 99.01% under the optimum conditions of 1174 °C, 86 min, and 12% carbon mass ratio. In addition, compared with the carbothermal reduction in air, the carbon mass ratio requirement is reduced by 10–20% in the inert atmosphere. The volatilisation mechanism of zinc, particularly the distribution and migration behaviour, was studied using X-ray diffraction and scanning electron microscopy–energy dispersive X-ray spectroscopy. The results showed that in the high-temperature section of the lead–zinc ore treatment, zinc sulphide and zinc oxide are transformed via synergistic reduction involving carbon and calcium to zinc, and the presence of iron and calcium in the form of sulphides leads to a decrease in sulphur dioxide formation. This study explores the efficient and green development and utilization of low-grade lead–zinc oxysulphide ore by pyrometallurgical method to provide theoretical support for its large-scale industrial treatment.

Sulfidation Roasting of Lead and Zinc Carbonate with Sulphur by Temperature Gradient Method

Lead Recovery from Zinc Leaching Residue by Flotation

Recovery of Zinc and Copper from Lead Slag by the Combined Process of Beneficiation and Roasting

Desulfurization Mechanism of Lead–Zinc-Bearing Hematite–Limonite Ore Through Oxidation Roasting Process

Thermodynamic analysis and process optimization of zinc and lead recovery from copper smelting slag with chlorination roasting

Extraction of Lead and Zinc from a Rotary Kiln Oxidizing Roasting Cinder

Phase Transformation Analysis and Process Optimisation of Low-Grade Lead–Zinc Oxysulphide Ore Carbothermal Reduction

A Novel Technology for Separating Copper, Lead and Zinc in Flotation Concentrate by Oxidizing Roasting and Leaching

Recovery of lead and silver from zinc acid-leaching residue via a sulfation roasting and oxygen-rich chlorination leaching method

Recovery of Zinc and Silver from Zinc Acid-Leaching Residue by Sulphation Roasting-Water Leaching of Zinc and Iron-Silver Chlorination Leaching Method

Volatilization Kinetics of Zinc from the Flotation Products of Low-Grade Lead–Zinc Oxide Ore during Carbothermic Reduction

Recovery of Zinc and Lead from Copper Smelting Slags by Chlorination Roasting

Thermodynamics Evaluation and Verification of High-Sulfur Copper Slag Composite Agglomerate in Oxidation-Roasting-Separation-Leaching Process

Anglesite and silver recovery from jarosite residues through roasting and sulfidization-flotation in zinc hydrometallurgy

Mechanochemical sulfidization of lead oxides by grinding with sulfur

Sulfidation of Smithsonite via Microwave Roasting under Low-Temperature Conditions

Synergetic Utilization of Zinc-Bearing Dust by Carbothermic Reduction-Roasting Process: Phase Transformation and Morphological Evolution

Study on the Migration and Release of Sulfur during the Oxidizing Roasting of High-Sulfur Iron Ore

Flotation Separation of High Sulfur Lead-Zinc Ore

Recovery of Copper, Lead and Zinc from Copper Flash Converting Slag by the Sulfurization-Reduction Process

Experimental Study on Activated Sulfur Selection from High Alkalinity Lead Zinc Flotation Tailings