Abstract:In this paper, an efficient route is developed for controllable synthesis of ordered mesoporous alumina (OMA) materials with variable pore architectures and high mesoporosity, as well as crystalline framework. The route is based on the nanocasting pathway with bimodal mesoporous carbon as the hard template. In contrast to conventional reports, we first realize the possibility of creating two ordered mesopore architectures by using a single carbon hard template obtained from organic-organic self-assembly, which is also the first time such carbon materials are adopted to replicate ordered mesoporous materials. The mesopore architecture and surface property of the carbon template are rationally designed in order to obtain ordered alumina mesostructures. We found that the key factors rely on the unique bimodal mesopore architecture and surface functionalization of the carbon hard template. Namely, the bimodal mesopores (2.3 and 5.9 nm) and the surface functionalities make it possible to selectively load alumina into the small mesopores dominantly and/or with a layer of alumina coated on the inner surface of the large primary mesopores with different thicknesses until full loading is achieved. Thus, OMA materials with variable pore architectures (similar and reverse mesostructures relative to the carbon template) and controllable mesoporosity in a wide range are achieved. Meanwhile, in situ ammonia hydrolysis for conversion of the metal precursor to its hydroxide is helpful for easy crystallization (as low as approximately 500 degrees C). Well-crystallized alumina frameworks composed of gamma-Al(2)O(3) nanocrystals with sizes of 6-7 nm are obtained after burning out the carbon template at 600 degrees C, which is advantageous over soft-templated aluminas. The effects of synthesis factors are demonstrated and discussed relative to control experiments. Furthermore, our method is versatile enough to be used for general synthesis of other important but difficult-to-synthesize mesoporous metal oxides, such as magnesium oxide. We believe that the fundamentals in this research will provide new insights for rational synthesis of ordered mesoporous materials.

An Environmentally Friendly Method for the Synthesis of Nano-Alumina with Controllable Morphologies

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Sol-Gel Synthesis of Alumina Using Inorganic Salt Precursor

Facile synthesis of nano-crystalline alpha-alumina at low temperature via an absolute ethanol sol-gel strategy

Facile synthesis of monodisperse aluminum nitride microspheres

Fabrication and Application of Alumina Nanoscale Ordered Array Template

Cleaner Synthesis of Mesoporous Alumina from Sodium Aluminate Solution

The Morphologically Controlled Synthesis and Application of Mesoporous Alumina Spheres

Novel approach for synthesis of boehmite nanostructures and their conversion to aluminum oxide nanostructures for remove Congo red.

Preparation and External Adsorption of Nano Alumina

Synthesis and Application of Hierarchically Structured Nano-Alumina

Facile Synthesis of Highly Thermal-Stable Doped Alumina with High Surface Area by Low Temperature Solid-State Reaction

A Novel Method To Synthesize Amorphous Silica−Alumina Materials with Mesoporous Distribution without Using Templates and Pore-Regulating Agents

Synthesis of Aluminum Nitride Using Sodium Aluminate as Aluminum Source

Microreactor-assisted Synthesis of Α-Alumina Nanoparticles

Morphological Control of Mesoporous Alumina Nanostructures Via Template-Free Solvothermal Synthesis

Controllable Synthesis Of Pbo Nano/Microstructures Using A Porous Alumina Template

Nano Alumina: A Review of the Powder Synthesis Method

Ultrasonic Synthesis of Silica−Alumina Nanomaterials with Controlled Mesopore Distribution Without Using Surfactants

Synthesis of nano α-alumina powders using hydrothermal and precipitation routes: a comparative study

Ordered Mesoporous Crystalline Gamma-Al2o3 with Variable Architecture and Porosity from a Single Hard Template.