Abstract:Since the discovery of ordered mesoporous silica, due to the wide application of alumina as adsorbents, catalysts and catalyst supports, great efforts have been devoted to the synthesis of mesoporous alumina. Unfortunately disordered structures with amorphous walls were fabricated in most cases. Recently, ordered mesoporous aluminas have been synthesized by a modified sol–gel route in the presence of block copolymers, aerosol-assisted self-assembly with use of block copolymers, nanocasting process with mesoporous carbon (CMK-3) as hard template, and evaporation-induced self-assembly (EISA). Furthermore, the potential applications of mesoporous alumina can only be maximized in the highly crystalline state. However, all syntheses of mesoporous alumina reported so far only lead to the fabrication of powders or films, and not of monolithic materials, which refers to uniform structures composed of interconnected macrocells. In particular, monolithic materials with hierarchically multiscale porosity is an extensive field of investigation. Such materials not only enable high surface areas and high chemical activity sites (associated with microor mesoporous structure), but also allow for processing bulky molecules/species efficiently with fast diffusion to and from the active sites within the mesopores (associated with macroporous structure). These features are of great interest for a wide range of applications such as separation and as supports for flow-through systems, e.g., catalysts and sensing. Until now only a few reports have been available where mesoporous metal oxide monoliths other than silica-based monoliths were prepared. To our knowledge, there has been no report on macroporous g-Al2O3 monoliths with ordered mesopores on the walls. Here we describe the synthesis of bimodal macroporous g-Al2O3 monoliths with highly ordered crystalline mesoporous walls. The general synthesis strategy is based on a simple sol–gel process by using a conventional polyurethane (PU) foam replication method combined with a triblock copolymer P123 as mesoporous structure-directing agents. The synthetic mechanism of the hierarchically porous aluminas can be described as follows (also see ESIw, Fig. S1). The primary sol is prepared with aluminium isopropoxide as the inorganic precursor, nitric acid as the acid adjustor, and P123 as the surfactant, and all of which dissolved in ethanol as a transparent solution. When the PU foam is impregnated into the sol solution, the sol enters into the interconnected macropore voids by capillary and wetting driving forces. Then during the solvent evaporation, cross-linked aluminium species can assemble with the triblock copolymer P123 to form the ordered mesophases on the interior surface of the PU struts, resulting in a solvent-evaporation-induced coating and selfassembly process. The factors governing this self-assembled formation of ordered mesostructures were studied. It was found that the temperature played an important role. After finely tuning this factor, 40 1C is found to be the optimized condition and was adopted in the present work. After final appropriate calcination, the PU sponge and P123 can be removed, and an effective replica of the PU sponge with mesoporous structured alumina monolith is obtained. As shown in the photographs of our typical samples (Fig. 1(a)), the as-made alumina materials retain the original uniform morphologies of the used PU foam with different shrinkages due to calcinations at various temperatures. A typical alumina monolith calcined at 550 1C is large in size, with a length of 2.0 cm, width of 1.9 cm and height of 0.6 cm. Its shrinkage is calculated to be about 28% in linear dimensions. The size of the monoliths can be easily adjusted, since the used PU foam with different geometries can be prepared simply by cutting it into the desired shapes and sizes. Representative scanning electron microscopy (SEM) images of the alumina monoliths calcined at different temperatures are shown in Fig. 1(b) and (c). Fig. 1(b) shows that the alumina materials calcined at 550 1C exhibit a macroporous structure with interconnected open pores of 400–600 mm in size and thickness of the pore walls of about 50 mm. After calcination at 900 1C, the samples retain a 3D uniform macrostructure with the size of the interconnected macropores reduced slightly (Fig. 1(c)) due to the shrinkage during the calcination process at higher temperature, which is in agreement with the observed slight decrease of size of the materials. It is reasonable to deduce that macropore size of the materials could be tuned by using commercially available PU foam with different pore diameters as replica templates. Fig. 2(a) shows the small-angle X-ray diffraction (XRD) patterns of the as-synthesized alumina materials. The sample calcined at 550 1C shows a very sharp diffraction peak around 1.21 and one weak peak around 2.11, which can be attributed Beijng National Laboratory for Molecular Science, State Key Laboratory of Rare Earth Materials Chemistry and Applications, PKU-HKU Joint Laboratory on Rare Earth Materials and Bioinorganic Chemistry, Peking University, 100871, Beijing, China. E-mail: yan@pku.edu.cn; Fax: +86 10 6275 4179; Tel: +86 10 6275 4179 w Electronic supplementary information (ESI) available: Detailed synthesis procedures and additional experimental results. See DOI: 10.1039/b912495k

Ordered Mesoporous Crystalline Gamma-Al2o3 with Variable Architecture and Porosity from a Single Hard Template.

Mechanochemical Nonhydrolytic Sol–Gel-Strategy for the Production of Mesoporous Multimetallic Oxides

A vesicle-aggregation-assembly approach to highly ordered mesoporous γ-alumina microspheres with shifted double-diamond networks.

Facile Synthesis for Ordered Mesoporous Gamma-Aluminas with High Thermal Stability

Hierarchical c-Al2O3 monoliths with highly ordered 2D hexagonal mesopores in macroporous wallsw

Synthesis of Ordered Macro-Mesoporous Mg-Al Composite Oxides with High Thermal Stability and Mechanical Strength

A non-template approach to fabricate mesoporous alumina with predefined morphology by solid-state transformation of Al-based metal–organic frameworks

Fabrication and Application of Alumina Nanoscale Ordered Array Template

Facile Synthesis of Ordered Mesoporous Alumina and Alumina-Supported Metal Oxides with Tailored Adsorption and Framework Properties

The Morphologically Controlled Synthesis and Application of Mesoporous Alumina Spheres

Synthesis of ordered mesoporous alumina with large pore sizes and hierarchical structure

Catanionic-Surfactant Templated Synthesis Of Organized Mesoporous Gamma-Alumina By Double Hydrolysis Method

High Surface Area, Mesoporous, Glassy Alumina with a Controllable Pore Size by Nanocasting from Carbon Aerogels.

Synthesis, Characterization and Catalytic Applications of Mesoporous Γ-Alumina from Boehmite Sol

Ordered Mesoporous Alumina with Tunable Morphologies and Pore Sizes for CO2 Capture and Dye Separation

Construction of the Mosaic Aluminophosphate Zeotypes Based on Nonclassical Crystallization and in Situ Selective Etching Strategies

Catanionic-surfactant templated synthesis of organized mesoporous γ-alumina by double hydrolysis method

Templated fabrication of biomorphic alumina-based ceramics with hierarchical structure

General Synthesis of 3D Ordered Macro-/Mesoporous Materials by Templating Mesoporous Silica Confined in Opals

Synthesis of Ordered Mesoporous Zr-Al Composite Oxides with Excellent Structural and Textural Properties and Extremely High Stability

A Novel Synthesis Route of Mesoporous γ-Alumina from Polyoxohydroxide Aluminum