Abstract:This paper deals with a systematic investigation on the synthesis of aluminium oxide starting from mono hydroxy aluminium oxide (boehmite, (AlOOH)) which in turn is synthesized from aluminium nitrate. Boehmite on heating forms γ, transitional alumina and α-alumina phases in the temperature range 400–600, 800–1050 and 1050–1100°C respectively. Calculation from XRD, using Scherer equation shows that γ-alumina has crystallite size in the range 5–10 nm, while δ and θ-alumina are in the range 10–20 nm and α-alumina is about ∼33 nm. The textural features of aqueous sol-gel boehmite samples calcined at various temperatures were analyzed by specific surface area measurements and adsorption isotherm features. Maximum specific surface area of 266 m2/g is observed for the precursor calcined at 400°C and a minimum of 5 m2/g at 1100°C. Total pore volume is maximum for the precursor calcined at 600°C (0.2653 cm3/g). Average pore size ranges from ∼3 nm (400°C) to ∼11 nm (1100°C). The adsorption isotherms also show a change from Type IV to Type II with increase in temperature showing difference in surface properties. The information from t-plots, pore size distribution and cumulative pore volume data also indicates differences in porosity features of boehmite on calcination. The adsorption isotherm and pore size distribution analysis show maximum microporosity at 400°C, while maximum mesoporosity is observed at 600°C. At higher temperatures, porosity decreases, even though small fraction of pores in the mesopore range is still retained. At 1100°C, there is structural transformation from transitional to α-alumina, with very low specific surface area ∼5 m2/g and pores in the size range of 11 nm. The various data presented in this study will be useful in the synthesis of alumina with tailor made properties.

Nano Alumina: A Review of the Powder Synthesis Method

Synthesis and sintering behavior of a nanocrystalline α-alumina powder

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Synthesis of α-Al2O3 Nanopowders at Low Temperature from Aluminum Formate by Combustion Process

Sinterable Alumina Powders

Approach toward Alpha Alumina Synthesis

Recent development in the synthesis of polymer nanocomposites based on nano-alumina

Synthesis of nano α-alumina powders using hydrothermal and precipitation routes: a comparative study

Nanostructured ceramic powders by hydrothermal synthesis and their applications

Synthesis and structural characterization of alumina nanoparticles

Elaboration of alumina-based materials by solution combustion synthesis: A review

Adsorption Isotherm and Pore Characteristics of Nano Alumina Derived from Sol-Gel Boehmite

Microstructures of Nanosized Alumina Powders Synthesized by Sol-Gel Method

PREPARATION AND CHARACTERIZATION OF ALUMINA NANOCRYSTALLINE POWDER BY COMPLEXING SOL-GEL METHOD

Ultrasonic Synthesis of Silica−Alumina Nanomaterials with Controlled Mesopore Distribution Without Using Surfactants

Development of a simple aqueous solution based chemical method for synthesis of mesoporous γ-alumina powders with disordered pore structure

Optical and structural properties of spherical-shaped boehmite and γ-alumina nanoparticles by ultrasonic-assisted hydrothermal method: the effects of synthesis route, calcination, and precursor concentration

Exploration of properties (crystallographic, morphological, optical) of nano cobalt aluminate synthesized by facile sol-gel method: Effects of sintering temperature

Preparation of Nano Powders by Sintering Process for Nanomaterials

Ultrasound As a Tool to Synthesize Nano-Sized Silica–Alumina Catalysts with Controlled Mesoporous Distribution by a Novel Sol–Gel Process

Latest Research on the Development of High-Quality Aluminum-Oxide Ceramics (Review). Part 2. Synthesis and Sintering of Nanopowders, Sol-Gel and Other Methods of Producing Finely Disperse and Fibrous Aluminum Oxide