Abstract:This study focuses on investigating the effect of ignition temperature for the combustion synthesis (CS) on the selective catalytic reduction of NOx with NH3 over Ti0.9Ce0.05V0.05O2−δ nanocomposites serial catalysts prepared by the solution combustion method. Ti0.9Ce0.05V0.05O2−δ-350°C showed the best SCR activity and N2 selectivity in a broad temperature window of 150–400°C, in which more than 83% NOx was reduced with the superior N2 selectivity above 95%. The influence of the ignition temperature for CS on the physical and morphological properties, the crystalline phase, the microstructure, the redox behavior, the oxidation state, the reactants adsorption capability, and the evolution of the surface nitrate and acid sites after the adsorption of NOx and NH3 was extensively investigated in detail using comprehensive characterization techniques including N2 physisorption, XRD, SEM, TEM, FTIR, EPR, and XPS. The increase of the ignition temperature, the decrease of the specific surface area, the total desorption pore volume, the surface fractal dimension, and the concentration of the chemisorbed oxygen, and the increase of the average pore diameter and the particle size, which may be the main reasons for the decline of the NOx removal efficiency and the N2 selectivity. In addition, the NOx/NH3-TPD results suggest that the Ti0.9Ce0.05V0.05O2−δ catalysts prepared at lower ignition temperatures could provide more chemisorption NOx and NH3 species, and simultaneously enhance the activation of both species that result in the improvement of the SCR activity. Furthermore, the in situ DRIFTS results indicate that the active monodentate nitrate and bridging nitrate species come from the NOx adsorption and that the ionic NH4+ bound to the BrØnsted acid sites are active species and essential for the SCR process. The increase of the ignition temperature decreases the key surface nitrate species and acid sites, and thus the relevant NH3-SCR activity and selectivity.

Solution Combustion Synthesis of Ti0.75Ce0.15Cu0.05W0.05O2−δfor Low Temperature Selective Catalytic Reduction of NO

Activation of Fast Selective Catalytic Reduction of NO by NH3 at Low Temperature over TiO2 Modified CuOX-CeOX Composites

C,N‐modified TiO2‐supported Mn–Ce–Cox‐based Catalyst for Low‐temperature NH3‐SCR

DRIFT Study of CuO-CeO₂-TiO₂ Mixed Oxides for NOx Reduction with NH₃ at Low Temperatures.

DRIFT Study of CuO–CeO2–TiO2 Mixed Oxides for NOx Reduction with NH3 at Low Temperatures

Highly Dispersed Surface Active Species of Mn/Ce/TiW Catalysts for High Performance at Low Temperature NH3-SCR

Speeding up low-temperature SCR with reactants-coupling dual catalytic sites

Improvement in Activity and Alkali Resistance of a Novel V-Ce(SO4)2/Ti Catalyst for Selective Catalytic Reduction of NO with NH3

A Ce–Cu–Ti oxide catalyst for the selective catalytic reduction of NO with NH3

Low-temperature Activity and Mechanism of WO3-modified CeO2-TiO2 Catalyst under NH3-NO/NO2 SCR Conditions

The Superior Performance of Nb-modified Cu-Ce-Ti Mixed Oxides for the Selective Catalytic Reduction of NO with NH3 at Low Temperature

Effect of Ignition Temperature for Combustion Synthesis on the Selective Catalytic Reduction of NO with NH3 over Ti0.9Ce0.05V0.05O2− Nanocomposites Catalysts Prepared by Solution Combustion Route

Improved K-Resistance of a Cu-Modified TiO2/CeO2 Catalyst for SCR of NOx at Low Temperatures

Revealing the Excellent Low-Temperature Activity of the Fe 1- x Ce x O δ -S Catalyst for NH 3 -SCR: Improvement of the Lattice Oxygen Mobility

The activity and characterization of CeO2-TiO2 catalysts prepared by the sol-gel method for selective catalytic reduction of NO with NH3.

The selective catalytic reduction of NO over Ce0.3TiOx-supported metal oxide catalysts

Ceria modified MnOx/TiO2 as a superior catalyst for NO reduction with NH3 at low-temperature

Effect of Synthesis Methods on Activity of V2O5/CeO2/WO3-TiO2 Catalyst for Selective Catalytic Reduction of NOx with NH3

Performance of a Novel CuSO4-CeO2/TiO2-SiO2 Catalyst for NO Reduction with NH3 at Low Temperature

CuOx and WOx modified CeO2-TiO2 with various morphologies for the selective catalytic reduction of NOx with NH3

Low-temperature selective catalytic reduction of NO on CeO2-CuO/Al2O3 catalysts prepared by different methods