Preparation of Mg-Ni hydrogen storage alloy powders by direct-current arc plasma method

Jianxin Zou,Haiquan Sun,Xiaoqin Zeng

DOI: https://doi.org/10.3969/j.issn.2095-2783.2014.06.002

2014-01-01

Abstract:Mg-Ni based ultrafine powders were prepared through the direct-current (DC)arc plasma method using the arc anode material which was obtained by mixing,ball milling and sintering procedures from Mg and Ni powders.The phase components, morphology and composition of the powders were analyzed by the means of XRD,TEM and ICP.XRD analyses reveal the forma-tion of Mg2 Ni after sintering the Mg and Ni powders.After arc plasma evaporation,Mg content increases and MgNi2 forms at the same time,indicating that Mg2 Ni decomposes into Mg and Ni during the arc evaporation and they react again to form Mg2 Ni and MgNi2 phases.ICP analysis shows that sintered Mg2 Ni can release more Ni during arc evaporation.TEM observation shows that those Mg particles have hexagonal shape with size ranging from 100 nm to 600 nm.While those Mg2 Ni nano grains,about 10-50 nm,attached on the Mg ultrafine particles.Such kind of microstructure will be helpful for improving the hydrogen sorption property of Mg.