Abstract:The ultrafine metallic ni (∼5 nm) was in situ formed in the MgH2Ni-EG nanocomposite by ball milling.The MgH2Ni-EG nanocomposite can still release extraordinary H2 of 7.03 wt.% within 8.5 min after 10 cycles.The cycle stability of the MgH2Ni-EG nanocomposite is also excellent.The evolution process of Ni(acac)2 has been systematically studied.It has been well known that doping nano-scale catalysts can significantly improve both the kinetics and reversible hydrogen storage capacity of MgH2. However, so far it is still a challenge to directly synthesize ultrafine catalysts (e.g., < 5 nm), mainly because of the complicated chemical reaction processes. Here, a facile one-step high-energy ball milling process is developed to in situ form ultrafine Ni nanoparticles from the nickel acetylacetonate precursor in the MgH2 matrix. With the combined action of ultrafine metallic Ni and expanded graphite (EG), the formed MgH2Ni-EG nanocomposite with the optimized doping amounts of Ni and EG can still release 7.03 wt.% H2 within 8.5 min at 300 °C after 10 cycles. At a temperature close to room temperature (50 °C), it can also absorb 2.42 wt.% H2 within 1 h It can be confirmed from the microstructural characterization analysis that the in situ formed ultrafine metallic Ni is transformed into Mg2Ni/Mg2NiH4 in the subsequent hydrogen absorption and desorption cycles. It is calculated that the dehydrogenation activation energy of the MgH2Ni-EG nanocomposite is also reduced obviously in comparison with the pure MgH2. Our work provides a methodology to significantly improve the hydrogen storage performance of MgH2 by combining the in situ formed and uniformly dispersed ultrafine metallic catalyst from the precursor and EG.

Preparation of the Mg<sub>2</sub>Ni compound from ultrafine particles and its hydrogen storage properties

Preparation and hydrogen storage properties of Mg<sub>2</sub>Ni intermetallic nanoparticles

Preparation of Mg2Ni Intermetallic Compound from Nanoparticles

Hydrogen storage in Mg2Ni(Fe)H4 nano particles synthesized from coarse-grained Mg and nano sized Ni(Fe) precursor

Preparation and Hydrogen Sorption Properties of a Ni Decorated Mg Based Mg@Ni Nano-Composite

Scaled-Up Synthesis of Nanostructured Mg-Based Compounds and Their Hydrogen Storage Properties

In situ formed ultrafine metallic Ni from nickel (II) acetylacetonate precursor to realize an exceptional hydrogen storage performance of MgH2Ni-EG nanocomposite

Phase-structure and Hydrogen Storage Behaviors of Mg+10％ Ni2P Composite Prepared by Reactive Ball-Milling

Preparation of Mg-based hydrogen storage materials from metal nanoparticles

Preparation and hydrogen storage properties of nanostructured Mg2Cu alloy

Synthesis and hydrogen storing properties of nanostructured ternary Mg–Ni–Co compounds

High-load Mg2Ni nanoparticle-carbon nanofiber composites for hydrogen storage

Nanoscale Ni as a catalyst in MgH2 for hydrogen storage material

Hydrogen storage in Mg2Fe(Ni)H6 nanowires synthesized from coarse-grained Mg and nano sized γ-Fe(Ni) precursors

Phase, Microstructure and Hydrogen Storage Properties of Mg–Ni Materials Synthesized from Metal Nanoparticles

Effect of in-situ formed Mg2Ni/Mg2NiH4 compounds on hydrogen storage performance of MgH2

Preparation and Hydrogen Storage Properties of Mg-20 Wt.% Mg<sub>2</sub>Ni<sub>0.8</sub>Cr<sub>0.2</sub> Composite with TiO<sub>2</sub> Nanoparticles

H 2 Plasma Reducing Ni Nanoparticles for Superior Catalysis on Hydrogen Sorption of MgH 2

Synthesis and hydrogen storage properties of Mg–10.6La–3.5Ni nanoparticles

Hydrogen storage properties of Mg-23.3wt.%Ni eutectic alloy prepared via hydriding combustion synthesis followed by mechanical milling

Hydrogen Storage Properties of Nanosized MgH<sub>2</sub>−0.1TiH<sub>2</sub>Prepared by Ultrahigh-Energy−High-Pressure Milling