Effect of in-situ formed Mg2Ni/Mg2NiH4 compounds on hydrogen storage performance of MgH2

Yaokun Fu,Zhenmin Ding,Shuqin Ren,Xinjun Li,Shuhua Zhou,Lu Zhang,Wenfeng Wang,Lailei Wu,Yuan Li,Shumin Han

DOI: https://doi.org/10.1016/j.ijhydene.2020.03.089

IF: 7.2

2020-10-01

International Journal of Hydrogen Energy

Abstract:Magnesium-based hydrogen storage materials (MgH2) are promising hydrogen carrier due to the high gravimetric hydrogen density; however, the undesirable thermodynamic stability and slow kinetics restrict its utilization. In this work, we assist the de/hydrogenation of MgH2 via in situ formed additives from the conversion of an MgNi2 alloy upon de/hydrogenation. The MgH2–16.7 wt%MgNi2 composite was synthesized by ball milling of Mg powder and MgNi2 alloy followed by a hydrogen combustion synthesis method, where most of the Mg converted to MgH2, and the others reacted with the MgNi2 generating Mg2NiH4, which produced in situ Mg2Ni during dehydrogenation. Results showed that the Mg2Ni and Mg2NiH4 could induce hydrogen absorption and desorption of the MgH2, that it absorbed 2.5 wt% H2 at 473 K, much higher than that of pure Mg, and the dehydrogenation capacity increased by 2.6 wt% at 573 K. Besides, the initial dehydrogenation temperature of the composite under the promotion of Mg2NiH4 decreased greatly by 100 K, whereas it is 623 K for MgH2. Furthermore, benefiting from the catalyst effect of Mg2NiH4 during dehydrogenation, the apparent activation energy of the composite reduced to 73.2 kJ mol−1 H2 from 129.5 kJ mol−1 H2.

energy & fuels,electrochemistry,chemistry, physical

What problem does this paper attempt to address?

The paper aims to address the issues related to the hydrogen storage performance of magnesium-based hydrogen storage materials (MgH₂). Specifically, MgH₂ has garnered significant attention due to its high theoretical hydrogen storage density (7.6 wt%), but its practical application is limited by its poor thermodynamic stability and kinetic performance. The paper improves the hydrogen absorption and desorption performance of MgH₂ by adding MgNi₂ alloy as a catalyst.

The main research contents include:
1. **Synthesis Method**: Mg powder and MgNi₂ alloy are mixed through ball milling and hydrogen combustion synthesis (HCS) to prepare MgH₂-16.7 wt% MgNi₂ composite material.
2. **Hydrogen Absorption and Desorption Performance**: Studies show that after adding MgNi₂, the MgH₂-16.7 wt% MgNi₂ composite material can absorb 4.5 wt% of hydrogen within 20 minutes at 473 K, which is significantly higher than the performance of pure MgH₂.
3. **Kinetic Performance**: By adding MgNi₂, the initial dehydrogenation temperature of MgH₂ is reduced by approximately 100 K, from the original 623 K to around 523 K.
4. **Catalytic Effect**: MgNi₂ forms Mg₂NiH₄ during the hydrogenation process and Mg₂Ni during the dehydrogenation process. These two intermediate phases can promote the hydrogen absorption and desorption process of MgH₂, significantly improving its kinetic performance.

In conclusion, the paper significantly enhances the hydrogen absorption and desorption rate and capacity of MgH₂ and reduces the required dehydrogenation temperature by introducing MgNi₂ as an additive. This research outcome is expected to promote the practical application of magnesium-based hydrogen storage materials.