Abstract:An yttria-stabilized zirconia (YSZ) (111) substrate is a promising candidate for the growth of c-plane InN due to its small lattice mismatch of 2.7%. Polarity control of InN (0001) films on YSZ substrates is a crucial issue for device fabrication because mixture of In-polar and N-polar InN will degrade device performance. We have recently found that thermal annealing of the YSZ (111) substrates leads to the formation of In-polar InN films. This phenomenon is probably caused by segregation of the Y atoms at the surfaces of the YSZ substrates [1]. In this presentation, we will discuss the polarity determination of c-plane InN films grown on YSZ (111) substrates based on the calculated adsorption energies for the In atom on the N-covered YSZ (111) surface. A cubic zirconia (111) slab is employed as the Y-segregation free substrate. For the Y-segregated substrate, all Zr atoms in the upper half of the zirconia in the cell were replaced with Y atoms. Firstly, adsorption energies of the In and N atoms on the YSZ surfaces are calculated. The large adsorption energy for N atoms compared with that for In atoms suggests that the first layer on the Y-segregated YSZ (111) surfaces should consist of N atoms. Calculations of the adsorption energies of an In atom on the N adatoms covering the surfaces was performed to investigate the polarity dependence of the stability of InN on YSZ. As shown in Fig.1, an In atom at the center of three N atoms (‘‘Hollow N’’) leads to In-polar InN, whereas an In atom on the top of a N atom (‘‘Top N’’) results in N-polar InN. According to the calculations shown in table 1, In-polar InN is more stable on the Y-segregated surfaces. On the other hand, the energy difference between the In-polar and N-polar InN on the segregation-free cubic zirconia surfaces is quite small. These data are quite consistent with the experimental results. [1] A. Kobayashi, K. Okubo, J. Ohta, M. Oshima and H. Fujioka, Phys. Status Solidi A 209, 2251 (2012). Substrate Adsorption energy of In

Selective Area Growth of InN Nanocolumns: Effect of Lattice Polarity

Polarity dependent strongly inhomogeneous In-incorporation in GaN nanocolumns

Comparative study of InN growth on Ga- and N-polarity GaN templates by molecular-beam epitaxy

Molecular Beam Epitaxy Growth of GaN, AlN and InN

Lattice-polarity-driven epitaxy of hexagonal semiconductor nanowires

Effects of film polarities on InN growth by molecular-beam epitaxy

Step-Flow Growth of InN on N-Polarity GaN Template by Molecular Beam Epitaxy with a Growth Rate of 1.3μm/h

Spontaneous nucleation and growth of GaN nanowires: Fundamental role of crystal polarity

Epitaxial Lateral Overgrowth of Nitrogen-Polar (0001̅) GaN by Metalorganic Chemical Vapor Deposition

Atomic‐Scale Mechanism of Spontaneous Polarity Inversion in AlN on Nonpolar Sapphire Substrate Grown by MOCVD

In Adlayers on C-Plane Inn Surfaces: A Polarity-Dependent Study by X-Ray Photoemission Spectroscopy

Polarity-induced selective area epitaxy of GaN nanowires

Nonpolar Growth And Characterization Of Inn Overlayers On Vertically Oriented Gan Nanorods

Inn{0001} Polarity by Ion Scattering Spectroscopy

Theoretical investigation of polarity determination for c-plane InN grown on yttria-stabilized zirconia (111) substrates

Selective area growth and characterization of GaN nanocolumns, with and without an InGaN insertion, on semi-polar (11–22) GaN templates

Polarity Control and Growth of Lateral Polarity Structures in Aln

Growth of Non-Polar A-Plane and Cubic InN on R-Plane Sapphire by Molecular Beam Epitaxy

Cost-effective Selective-Area Growth of GaN-based Nanocolumns on Silicon Substrates by Molecular-Beam Epitaxy

Behaviours of the lattice-polarity inversion in the AlN growth on the c-Al2O3(0001) substrates by ammonia-free high temperature metalorganic chemical vapor deposition

Atomic‐Scale Mechanism of Spontaneous Polarity Inversion in AlN on Nonpolar Sapphire Substrate Grown by MOCVD (Small 16/2022)