Abstract:The formation of titanium silicides has been studied using simultaneous in situ x-ray diffraction with millisecond time resolution and sheet resistance measurements. The effect of a Mo interposed layer between Ti films and Si substrate was investigated by varying the thickness of the Mo interlayer from 0 (Ti/Si) to 1.8 nm (Ti/Mo/Si). The thickness of Ti was kept to 55 nm for all samples. Both isothermal annealing and ramp annealing in helium were performed in order to study the mechanism of silicide formation. While C49 TiSi2 was the only disilicide found after annealing Ti/Si at 650 °C for 20 min, C54 TiSi2 was readily formed in the presence of Mo. The formation of C49 TiSi2 was not observed with a 1.8 nm thick Mo interlayer. Instead, there was indication that C40 (Mo,Ti)Si2 was formed. In addition, broad diffraction peaks, weak in intensity, could be all assigned to Ti5Si4. However, the presence of Ti5Si4 alone did not induce the formation of C54 TiSi2. Even with a 20 °C increase in isothermal annealing temperature to 670 °C for 20 min, the presence of Mo was found to be a necessity for the formation of C54 TiSi2. When annealed in nitrogen, instead of helium, the formation of surface titanium nitride competes with the formation of silicides. The formation of C54 TiSi2 was even suppressed in the sample with a 1.8 nm Mo interlayer when annealed at 650 °C in nitrogen. The formation of Ti5Si4 and the role it plays in the formation of other silicides (C40, C49, and C54) are discussed on the basis of simple crystallographic considerations. The effect of a Mo interlayer and/or ramp-rate on the formation of C40 (Mo,Ti)Si2 and C49 TiSi2 is discussed in conjunction with variations of the preferential orientation of C54 TiSi2 films.

Effect of Ion Irradiation on the Formation of Ni, Cr and Pt Silicide

Role of Carrier Concentration in Swift Heavy Ion Irradiation Induced Surface Modifications

Nanopatterning of metal-coated silicon surfaces via ion beam irradiation: Real time x-ray studies reveal the effect of silicide bonding

A comparative study of C, N and Xe pre-amorphization implantation processes for improving the thermal stability of NiSi films

Thermal stability, phase and interface uniformity of Ni-silicide formed by Ni–Si solid-state reaction

Effect of Pt Interlayer on Thermal Stability of NiSi Films

Nanoscale η-NiSi formation via ion irradiation of Si/Ni/Si

Pt interlayer effects on Ni germanosilicide formation and contact properties

Microstructure Evolution of the Interface in SiCf/TiC-Ti3SiC2 Composite under Sequential Xe-He-H Ion Irradiation and Annealing Process

X-ray photoelectron spectroscopy study of NiSi formation on shallow junctions

Role of Ni, Si and P on the formation of solute-rich clusters under irradiation in Fe-Cr alloys

NiPt silicide agglomeration accompanied by stress relaxation in NiSi(010) ∥ Si(001) grains

Enhanced Thermal Stability of NiSi Films on Si(111) Substrates by a Thin Pt Interlayer

Thermal Stability and Interface Improvement of Thin Nisige by C+ Ion Implantation

Effect of Annealing Temperature on the Formation of Silicides and the Surface Morphologies of PtSi Films

In Situ Characterization of Titanium Silicide Formation: the Effect of Mo Interlayer, Temperature Ramp-Rate, and Annealing Atmosphere

First-principles Investigation on the Composition of Ni-Si Precipitates Formed in Irradiated Stainless Steels

Ti-capping and heating ramp-rate effects on Ni-silicide film and interface

Amorphization Implant Technology in NiSi SALICIDE Process

Influence of Ti Interlayer on Untrathin Ni Film Silicidation

Ion Mixing and Demixing in the Au-Si System