Abstract:The surface mechanical attrition treatment was taken to fabricate the gradient structure in AZ31 magnesium alloy sheet. Microstructural investigations demonstrate the formation of dual gradients with respect to grain size and orientation, where the microstructural sizes decreased from several microns to about 200 nm from center area to treated surface, while the c-axis gradually inclined from being vertical to treated plane towards parallel with it. According to tensile results, the gradient structured sample has yield strength of 305 MPa in average, which is increased by about 4 times when compared with its coarse-grained counterpart. Meanwhile, contrary to quickly failure after necking in most traditional magnesium alloys, the failure process of gradient structure appears more gently, which makes it has 6.5% uniform elongation but 11.5% total elongation. The further comparative tensile tests for separated gradient layers and corresponding cores demonstrate that the gradient structured sample has higher elongation either in uniform or in post-uniform stages. In order to elucidate the relationship between mechanical properties and deformation mechanisms for this dual gradient structure, the repeated stress relaxation tests and pole figure examinations via X-ray diffraction were conducted in constituent gradient layer and corresponding core, as well as gradient structured sample. The results show that the pyramidal dislocations in dual gradient structure are activated through the whole thickness of sample. Together with the contribution of grain-size gradient, more dislocations are activated in dual gradient structure under tensile loading, which results in stronger strain hardening and hence higher tensile ductility.

Anisotropy of the Crystallographic Orientation and Corrosion Performance of High-Strength AZ80 Mg Alloy

Effect of grain size and crystal orientation on the corrosion behavior of as-extruded Mg-6Gd-2Y-0.2Zr alloy

Study of grain orientation effect on the corrosion behavior of biocompatible magnesium alloy Mg-2Zn-0.5Ca

High corrosion resistance and weak corrosion anisotropy of an as-rolled Mg-3Al-1Zn (in wt.%) alloy with strong crystallographic texture

Microstructure Evolution and Mechanical Properties of AZ80 Mg Alloy during Annular Channel Angular Extrusion Process and Heat Treatment

Effect of grain size uniformity and crystallographic orientation on the corrosion behavior of Mg-2Zn-1Al bar

Microstructure evolution and mechanical anisotropy of AZ80-Ag magnesium alloy: Effect of isothermal semi-closed die forging and subsequent aging

The Effect of Texture on the Corrosion Behavior of AZ31 Mg Alloy

Corrosion behavior and mechanical properties of extruded low-alloyed Mg−0.5Bi−0.5Y−0.2Zn alloy

Elucidating the dependence of corrosion behavior and mechanical property on the grain structure of low-temperature as-extruded Mg–Zn–Ca–Zr alloy

The synergistic effects of texture and continuous precipitates on the corrosion resistance of AZ80 magnesium alloy

Effect of texture evolution on corrosion resistance of AZ80 magnesium alloy subjected to applied force in simulated body fluid

Anisotropic Corrosion Behavior of Hot-Rolled Mg-8 Wt.%li Alloy

Effects of orientation on the fatigue crack growth behaviors of the ZK60 magnesium alloy in air and PBS

Investigation on corrosion behavior and mechanical properties of an extruded Mg-Zn-Al-Sn-Mn alloy

Mechanical Properties and Deformation Mechanism of Mg-Al-Zn Alloy with Gradient Microstructure in Grain Size and Orientation

Modulation of corrosion properties by heat treatment and extrusion with mechanism analysis of high mechanical strength Mg-5.6Dy-3.1Ni alloy

Mechanical Properties and Microstructures of Mg-Al-Zn Alloys with High Aluminum Contents

Influence of Anodic Oxidation on the Organizational Structure and Corrosion Resistance of Oxide Film on AZ31B Magnesium Alloy

Investigation on the anisotropy of mechanical properties along different orientations of an AZ31 hot-extrusion bar

Effect of ZrSiO4 Concentration on the Microstructure and Corrosion Resistance of MAO Coatings Formed on AZ91 Magnesium Alloy