Effect of deep cryogenic treatment on microstructures and mechanical properties of automotive 6063Al alloy
Guirong Li,Zili Cao,Hongming Wang,Yurong Ye,Ming Xiong,Kang Dong,Shouzuo Guo,Pengjie Zhou
DOI: https://doi.org/10.1007/s10853-024-09505-8
IF: 4.5
2024-03-24
Journal of Materials Science
Abstract:In this paper, the effect of deep cryogenic treatment (DCT) on the microstructure and properties of automotive 6063 aluminum alloy at different times was investigated with automotive 6063 aluminum alloy as the research object. The results show that under the conditions of deep cryogenic treatment, the lattice distortion occurs in the alloy matrix microstructure, and the resulting internal stress promotes the large proliferation of dislocations within the alloy and the increase of dislocation density; meanwhile, after the deep cryogenic treatment, the deformed grains are transformed into recrystallized and sub-crystals structural grains, the grains are refined, and the size of the grains is refined from the original 25.2 μm to 20.3 μm, with fine equiaxed crystals. Among them, the mechanical properties of the DCT36h specimen were the best, and its hardness, tensile strength, yield strength and elongation reached 142.44 HV, 328.32 MPa, 177.42 MPa, and 29.29%, which were 34.17%, 5.62%, 11.10%, and 32.77% higher than the original sample, respectively. We believe that the main mechanism for the increase in toughness is multiple reinforcement such as dislocation strengthening, grain refinement strengthening, precipitated phase strengthening and texture strengthening.
materials science, multidisciplinary