Effects of cryogenic deformation on the microstructure and mechanical properties of high-strength aluminum alloys

Dang Wang,Shiquan Huang,Youping Yi,Hailin He,Chen Li

DOI: https://doi.org/10.1016/j.matchar.2022.111831

IF: 4.537

2022-01-01

Materials Characterization

Abstract:7A85 aluminum alloy forgings were compressed at 10% to 30% deformation at room and cryogenic temperatures, followed by solid-solution treatment, water quenching, 3% cold deformation, and two-stage aging. The results indicated that cryogenic deformation increased coarse second-phase particle fragmentation and led to massive dislocation proliferation, which facilitated particle dissolution due to the formation of more interfaces and dislocation-promoted dissolution. These increased the driving force for aging precipitation and produced denser matrix precipitates and narrower grain boundary precipitate-free zones. Meanwhile, numerous dislocations provided more nucleation sites for recrystallization and thus refined grains during solution treatment. The grains were refined from 500 mu m in the undeformed state to an average size of 35 mu m under 20% cryogenic deformation. The excessive dislocation energy and stored deformation energy at 30% deformation caused recrystallized grain growth. The optimal mechanical properties were obtained at 20% cryogenic deformation with an ultimate tensile strength, yield strength, and elongation of 499 MPa, 435 MPa, and 13.1%, which were respectively 1.6%, 2.1%, and 37.9% higher than those of the undeformed sample.