Abstract:High cycle fatigue (HCF) behaviours of cast aluminium alloys at room temperature (RT) and elevated temperatures are examined in this study. The results show that fatigue life significantly decreases at 300 ℃ compared to RT, while the decline at 200 ℃ is relatively small. The coefficient of variation (CV) in fatigue life increases with decreasing load levels at all temperatures. The fracture analysis reveals that pores are primary sites for crack nucleation at both RT and 200 ℃, while cracks also nucleate from hard particles and slip bands at 300 ℃, with the presence of multiple nucleation sites. Correlation analysis shows that the temperature and load level have a comparable impact on the uncertainty in fatigue life, while the effect of crack nucleation defect size is lower than temperature and load level. Fatigue life models were established using linear elastic fracture mechanic (LEFM) and artificial neural network (ANN), respectively, with the former showing lower accuracy due to its inability to capture non-linear material softening at 300 ℃, and the latter demonstrating higher performance with the majority of predictions falling within ± 2.5X scatter bands. Finally, the omni-direction inference between cause and effect is performed using the Bayesian network (BN), which can predict fatigue life distribution interval probabilistically, achieving a balance in predictive and explanatory purposes well.

Fatigue Crack Growth Testing and Evaluation for Aluminum Alloys at Temperatures of 25°C and −70°C

Modelling Crack Propagation in Aluminium-Alloys 2524-T3 and 7050-T7452 Subjected to Fatigue Loading at Low Temperature

Testing and Evaluation for Fatigue Crack Propagation of Ti-6Al-4V/ELI and 7050-T7452 Alloys at High Temperatures

Modified Model for Evaluating Fatigue Behaviors and Lifetimes of Notched Aluminum-Alloys at Temperatures of 25°C and −70°C

Temperature Effect on Crack Propagation Properties of Aluminum Alloys in Aircraft

Environmentally-assisted Fatigue Crack Growth in AA7050-T73511 Al Alloy and AA2050-T84 Al-Cu-Li Alloy

Physical essence of long fatigue crack growth behavior for aluminum-lithium alloy

The Behavior of Fatigue Crack Initiation and Propagation in AA2524-T34 Alloy

Effect of Cryogenic Treatment on the Fatigue Crack Propagation Behavior of 7075 Aluminum Alloy

Fatigue Crack Growth Behavior of Al-4.41Cu-0.69Mg-0.64Si-0.52Mn Alloy Forged at Different Temperatures

Effects of aging temperature on microstructure and high cycle fatigue performance of 7075 aluminum alloy

Effect of temperature and corrosive environment on cyclic fatigue and final fracture behavior of 2524 aluminum alloy

Influence of Environment and Creep on Fatigue Crack Growth in a High Temperature Aluminum Alloy 8009

Fatigue Crack Growth of Alloy 7050-T7451 Plate in L-S Orientation

Study on High Cycle Fatigue Behaviours and Modelling of Cast Aluminium Alloy at Elevated Temperatures

The Microstructure and Fatigue Initiation of an AA2524-T34 Aluminum Alloy

Fatigue and fracture behavior of an aluminum-lithium alloy 8090-T6 at ambient and cryogenic temperature

Fatigue Failure Analyses On A Ti-45al-8nb-0.2w-0.2b-0.1y Alloy At Different Temperatures

Fatigue Fracture Analysis on 2524 Aluminum Alloy with the Influence of Creep-Aging Forming Processes

Fatigue cracking behavior and life assessment of TC11 titanium alloy in very high cycle regime at two working temperatures

Effect of temperature on the fatigue cracking mechanisms in A356 Al alloy