Abstract:SiC/SiC composites, prepared by reactive melt infiltration (RMI), exhibit exceptional properties. However, the presence of residual Si in the composite matrix can significantly compromise their high-temperature mechanical properties. Addressing the issue of high-content residual Si aggregation remains a crucial focus of research in order to fully unlock the application potential of SiC/SiC composites prepared by RMI. In this work, a special porous carbon (C g ) is successfully synthesized and introduced into the porous 2D SiC/SiC composites prepared by CVI. The unique pore structure of the SiC/SiC-C g is thoroughly analyzed, along with its liquid Si infiltration process. The difference in coefficient of thermal expansion (CTE) between SiC and C g can cause thermal stress, which can destory the C g structure. Consequently, the C particles detach from the C g skeleton and react with liquid Si to create SiC. This process effectively separates residual Si and helps alleviate the negative effects of residual Si aggregation. The microstructure and phase distribution of SiC/SiC composites obtained by liquid Si infiltrating different C structures are investigated and compared, and it demonstrates the positive effect of C g on the uniform phase distribution of matrix in the composites. The as-received SiC/SiC composites possess a density of 2.94 g/cm 3 with open porosity of 1.23%, and a flexural strength of 808.7±10.2MPa, a fracture toughness of 25.5±1.8MPa·m 1/2 , a tensile strength of 317.4±12.4MPa and a proportional ultimate stress of 157.33±4.1MPa. Acoustic emission (AE) and digital image correlation (DIC) technology are used to study the special mechanical behavior of composites.

Mechanical Properties Of Carbon/Silicon Carbide Composites Materials Bolts

Influence of Si and SiC Coating on the Microstructures and Mechanical Properties of C/C Bolts

Influence of SiC Coating Thickness on Mechanical Properties of SiCf/SiC Composite

Influence of Design Parameters on Mechanical Behavior of Multi-Bolt, Countersunk C/SiC Composite Joint Structure

Mechanical Property and Ballistic Performance of Silicon Carbide

Microstructure and mechanical properties of SiC f /SiC composite prepared by chemical vapor infiltration

Design, Fabrication, and Mechanical Properties of T-700TM Multiaxial-Warp-Knitting–Needled–C/SiC Composite and Pin

Tensile Mechanical Behavior and Failure Mechanism of a Plain-Woven SiCf/SiC Composites at Room and Elevated Temperatures

Sandwich-structured C/C-SiC Composites Fabricated by Electromagnetic-Coupling Chemical Vapor Infiltration

Study on Failure Characteristics of Typical Rivet Connections of C/SiC Composites

Binary Binder for Cf/C-SiC Composites with Enhanced Mechanical Property

A novel porous carbon synthesized to serve in the preparation of highly dense and high-strength SiC/SiC by reactive melt infiltration

Structure–property relationships of SiC reinforced advanced Al–Zn–Mg–Cu alloy

Fabrication process and mechanical properties of C/SiC corrugated core sandwich panel

Mechanical and tribological properties of C/C–SiC ceramic composites with different preforms

Bending and Thermal Expansion Properties of 2.5D C/SiC Composites

Bending and Thermal Expansion Properties of 3D-C_f/sic Composites

Mechanical and ablation properties of 3D orthogonal woven C/C-SiC composite based on high-solid-loading slurry impregnation

Mechanical Properties of Interfaces between Mg and SiC: An Ab Initio Study

Effect of SiC content on the mechanical behaviour of a three-dimensional needled C/SiC composite

Interfacial Reactions and Mechanical Properties Studies of C-Coated and C/B4C Duplex-Coated SiC Fiber-Reinforced Ti2AlNb Composites