Abstract:Industrial interest in wrought heat-treatable aluminium-lithium (Al–Li) based alloys dates back to around 1919 in Germany. However the exploitation of these alloys has historically been limited by their mechanical property anisotropy and concerns over their localized corrosion resistance and temperature stability. Recently, in the last ten years, alloy and process development has resulted in alloy compositions and thermomechanical treatments that potentially can overcome these issues. To put these developments in perspective we have reviewed the corrosion characteristics of first, second and third generation alloys with an emphasis on localized corrosion (intergranular and exfoliation) and stress corrosion cracking (SCC).Intergranular corrosion susceptibility of Al–Li–Cu and Al–Li–Cu–Mg alloys increases with copper content, and the depth of attack increases with ageing, i.e. UA<PA<OA. For alloys that contain zinc the mode of attack is less truly intergranular and more intra-granular or inter-subgranular in nature. Susceptibility to exfoliation corrosion has a similar temper dependence when assessed by conventional EXCO testing, but not following either exposure to a “real-life” outdoor marine environment or to a less aggressive test such as MASTMAASIS. In these tests there are two regimes of exfoliation susceptibility corresponding to under- and over-aged tempers, and an intermediate regime, including peak-aged tempers, with an improved resistance, i.e., UA>PA<OA.SCC initiation from smooth surfaces is rare for copper-free Al–Li alloys irrespective of temper or whether exposure is under continuous or alternate immersion conditions. For copper-containing alloys, initiation remains difficult for smooth specimens under continuous immersion conditions, but occurs readily under conditions of alternate immersion. It is likely that crack initiation is controlled by an anodic dissolution dominated process, but crack propagation may be controlled by either anodic dissolution or a hydrogen related process.Test results reviewed to date on thin plate samples show that the lower lithium content third generation Al–Li alloys, with suitable zinc and/or silver additions and thermomechanical processing can provide an acceptable resistance to localized corrosion (IGC and Exfoliation) and SCC in near to peak aged tempers. For this conclusion to apply to thicker products (>~30 mm) further analysis of corrosion test results is required.

Corrosion and Potentiostatic Polarization of an Al-Cu-Li Alloy under Tensile Stress

Enhancing Stress Corrosion Cracking Resistance of Low Cu-Containing Al-Zn-Mg-Cu Alloys by Aging Treatment Control

In-situ electrochemical analytical effect of aging treatment on stress corrosion behavior of Al–Zn–Mg–Cu aluminum alloy

Stress corrosion behavior and microstructure analysis of Al-Zn-Mg-Cu alloys friction stir welded joints under different aging conditions

Electrochemical Evaluation of Stress Corrosion Cracking Susceptibility of Ti-6Al-3Nb-2Zr-1Mo Alloy Welded Joint in Simulated Deep-Sea Environment

An Investigation of Corrosion-Induced Stress During SCC

Corrosion and Stress Corrosion of Aluminum–Lithium Alloys

Stress Corrosion Cracking of Copper–Nickel Alloys: A Review

Influence of AC/DC on stress corrosion cracking of Ti-6Al-3Nb-2Zr-1Mo alloy in simulated marine solution

Stress corrosion cracking of TC4 ELI alloy with different microstructure in 3.5% NaCl solution

Correlations among stress corrosion cracking, grain-boundary microchemistry, and Zn content in high Zn-containing Al–Zn–Mg–Cu alloys

Localized corrosion at nm-scale hardening precipitates in Al-Cu-Li alloys

Enhanced stress corrosion cracking resistance and electrical conductivity of a T761 treated Al-Zn-Mg-Cu alloy thin plate

The Localized Corrosion and Stress Corrosion Cracking of a 6005A-T6 Extrusion Profile

Effects of Aging Treatment on Corrosion Behavior of a Tensile Deformed Al-Cu-Mn-Fe-Zr Alloy in 3.5% NaCl Solution

Effect of Organizational Evolution on the Stress Corrosion Cracking of the Cr-Co-Ni-Mo Series of Ultra-High Strength Stainless Steel

Synergistic Effects of Corrosion and Slow Strain Rate Loading on the Mechanical and Electrochemical Response of an Aluminium Alloy

Corrosion behavior and electrochemical properties of carbon steel, commercial pure titanium, copper and copper–aluminum–nickel alloy in 3.5% sodium chloride containing sulfide ions

In-situ visualization of corrosion behavior of Al CoCrFeNi high-entropy alloys during electrochemical polarization

Time-varying electrochemically heterogeneous entities during the micro-galvanic corrosion associated with nanoscale precipitates in an Al-Cu-Li alloy

Effect of NaCl concentration, pH value and tensile stress on the galvanic corrosion behavior of 5050 aluminum alloy