Abstract:In the past, Mg-Zn alloys prepared by a two-step manufacturing process of casting plus extrusion have been demonstrated to be a good candidate for biodegradable applications. But, studies on fabricating of Mg-Zn alloys with a single step process of squeeze casting capable of producing porosity-free Mg alloys, which can reduce the cost, are limited. In the present work, Zinc (Zn) addition varying from 1.0 up to 10.0 wt. % was introduced into liquid magnesium. The alloyed liquid was squeeze cast under an applied pressure of 90 MPa. The results of mechanical testing on the squeeze cast Mg-Zn alloys shows that Zn is an effective additive for enhancing their mechanical properties, specifically, tensile and yield strengths at room temperature, but reducing the elongation. While the Zn addition rises from 1.0 to 10.0 wt.%, the ultimate tensile and yield strengths increases to 181.0 MPa and 105.0 MPa from 140.7 MPa and 39.3 MPa, while the elongation-to-failure (e f ) decreases to 3.7% from 6.2%, respectively. The reveal of the as-cast grain structure by an optical microscope (OM) indicates that the high Zn content reduces grain sizes considerably. The microstructures analyzed by a scanning electron microscope (SEM) with the energy dispersive spectroscopy (EDS) show that the secondary MgZn phase forms once Zn is introduced in sufficient amount. The grain refinement and the massive presence of the secondary MgZn phase at the boundaries of the refined grains should be responsible to the enhancement of the strengths and the reduction in the elongation. The developed pressurized casting without employing secondary manufacturing processes such as extrusion or heat treatment exhibits its advantages to enhance the mechanical properties of the Mg alloys with high Zn content over conventional fabrication processes, since high Zn-containing Mg alloys have a long freezing range and tend to form microshrinkage porosity.

Microstructure and Mechanical Properties of Squeezing Casting Mg-Nd-Gd-Zn-Zr Alloy

Experimental study of squeeze casting of ZK60 magnesium alloy

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Microstructure and Mechanical Properties of Squeeze Casting Quasicrystal Reinforced AZ91D Magnesium Matrix Composites

Influence of Pressure and Temperature on Microstructure and Mechanical Behavior of Squeeze Cast Mg-10Gd-3Y-0.5Zr Alloy

Study on Microstructure Distribution of Al-Cu-Mg Alloy in Squeeze Casting Process

Microstructure and mechanical properties of Mg–4Al–4Nd–0.5Zn–0.3Mn alloy

Squeeze Cast Mg-Zn Alloys for Bioapplications: Tensile Properties and Microstructure

Microstructure and Mechanical Properties of Mg–3.0Y–2.5Nd–1.0Gd–x Zn–0.5Zr Alloys Produced by Metallic and Sand Mold Casting

Microstructure and Mechanical Properties of Squeeze Cast Al-5 Mg-3Zn-1Cu-1Si Alloy along Cross Section

Microstructure and Mechanical Properties of Mg-Gd-Sm-Zr Alloy

Microstructure and Mechanical Properties of As-Cast and Extruded Mg–8Li–3Al–2Zn–0.5Nd Alloy

Effects of Pressure and Aging Treatment on Microstructures and Mechanical Properties of Rheo-Squeeze Casting Mg–3Nd–0.2Zn–0.4Zr Alloy

Microstructure and Mechanical Properties of Al-5Cu-4.5Mg-2.5Zn Squeeze Cast Alloy

The Research of Microstructure and Mechanical Properties of Mg–7Gd–3Y–1Nd–0.5Zn–0.5Zr (wt%) Alloy

Microstructures and Mechanical Properties of As-Cast and As-Extruded Mg-4.50zn-1.13ca (wt%) Alloys

Microstructure and Properties of Squeezing Casting Mg-9Gd-1Y-0.5Zr Alloy Piston

Microstructure evolution and mechanical properties of an ultra-high strength casting Mg–15.6Gd–1.8Ag–0.4Zr alloy

Effect of Mg addition on microstructure and mechanical properties of Al-Si-Cu-Fe alloy with squeeze casting

Microstructure and mechanical properties of squeeze-cast Al−5.0Mg−3.0Zn−1.0Cu alloys in solution-treated and aged conditions