Abstract:Direct electrodeposition (ECD) process of copper film on ultra-thin molybdenum film is investigated in both copper sulfate - sulfuric acid (CuSO4 - H2SO4) acidic bath and copper sulfate - ethylenediamine (CuSO4 - En) neutral bath (pH=7.5). The neutral electrolyte containing 0.03M CuSO4 and 0.06M En was chosen to avoid excessive corrosion of Mo and introduction of other ions. The complexing effect of En affects the electrodeposition process of Cu on Mo. Potentiodynamic polarization curves and scanning electron microscopic characterization show that Cu can be electroplated in CuSO4 - En bath with lower corrosion rate, greater nucleation density and shorter fully-covering time than that in CuSO4 - H2SO4 bath. The fitting results of current-time transients using Scharifker and Hill's model support the instantaneous nucleation and growth of Cu on Mo in both CuSO4 - H2SO4 bath and CuSO4 - En bath (with background electrolyte) at the initial stage of electrodeposition. By using an optimized two-step plating process (at the current density of 8mA/cm2 in the first step for a short time and 4mA/cm2 in the second step), the resistivity of direct ECD Cu on Mo was almost the same to that of ECD Cu on Cu/Mo in the same plating bath. Display Omitted The direct electrodeposition of Cu on Mo in neutral bath was reported originally.Corrosion rate of Mo is much lower in neutral bath than that in acidic bath.Hemispherical Cu nuclei are achieved in neutral bath rather than dendritic ones.The density Cu nuclei on Mo in neutral bath is much higher than that in acid bath.A two-step plating process was applied to lower the resistivity of direct ECD Cu.

Electroless Deposition of Cu with Solutions Containing Either Mg2+ or Pd2+ Ions

Experiment Study of Laser Thermal Enhanced Electrochemical Deposition

Electroless Cu Deposition Process on TiN for ULSI Interconnect Fabrication Via Pd/Sn Colloid Activation

Acidic Electroless Cu Deposition in Cuso4-Nh4f Solution

Electroless Copper Deposition for Ultralarge-Scale Integration

Electroless Deposition Of Copper Alloy In The Peg Additive

Electrodeposition of Extremely Cu-Rich CuPd Bimetallic Nanoparticles from an Amide-Type Hydrophobic Protic Ionic Liquid

Study of Direct Cu Electrodeposition on Ultra-Thin Mo for Copper Interconnect

Atomic layer deposition of copper and copper silver films using an electrochemical process

Behavior of Electroless Cu Deposition in CuSO[sub 4]-HF Solution

Dependency of Deposition Behavior, Microstructure and Properties of Cold Sprayed Cu on Morphology and Porosity of the Powder

Focused electron beam induced deposition of copper with high resolution and purity from aqueous solutions

Morphology Behavior of Copper Films Deposited after Wet Surface Treatment on Polished Alumina

Electrochemical Investigation of Pd-Free Electroless Co-Based Capping Layers on Cu Surfaces

Electrodeposition of Copper with Ultra-large Grains and Good Conductivity

Electrodeposition of copper on glassy carbon and palladium from choline chloride - ethylene glycol deep eutectic solvent

Cathodic Corrosion of Cu Substrates as a Route to Nanostructured Cu/M (M=Ag, Au, Pd) Surfaces

Electrodeposition, Structural, and Corrosion Properties of Cu Films from A Stable Deep Eutectics System with Additive of Ethylene Diamine

Plating Uniformity of Bottom-Up Copper Pillars and Patterns for Ic Substrates with Additive-Assisted Electrodeposition

Temperature-sensitivity of coating copper on sub-micron silicon carbide particles by electroless deposition in a rotation flask

Electrodeposition of Superhydrophobic Cu Film on Active Substrate from Deep Eutectic Solvent