Influence of nitrogen pre-implantation on deuterium retention in tungsten

liang gao,w jacob,p wang,u von toussaint,a manhard
DOI: https://doi.org/10.1088/0031-8949/2014/T159/014023
2014-01-01
Physica Scripta
Abstract:The influence of nitrogen (N) pre-implantation on the deuterium (D) retention in tungsten (W) at different temperatures was investigated. Bulk W samples were exposed to D plasma with a fluence of 1 x 10(24) D m(-2) with or without nitrogen pre-implantation at 300 and 500 K, respectively. Nuclear reaction analysis was applied for the determination of N content and D retention in the near surface. Optical microscopy was used to investigate the surface modification by blistering after implantation. It is shown that the W: N layers formed during the N pre-implantation play very different roles in D retention and blistering in the samples at different temperatures. At 500 K, the W: N layer seems to enhance D diffusion into the bulk by suppressing D loss from the surface, which results in a much higher D concentration in the bulk and larger blisters than without N pre-implantation. At 300 K, the effect of this layer is much less pronounced than that at 500 K.
What problem does this paper attempt to address?