Abstract:Surface modification, sputtering erosion and deuterium (D) retention were investigated of tungsten (W) and W-1 wt.% La2O3 (WL10) that were exposed to pure D plasma and D plasma with different impurities (He, N2, Ar). After the plasma exposure, the surface of WL10 is covered by blisters with various shapes, and their size and density increase with D fluence. When the fluence was higher than 8.6 x 1024 D m-2, the blister rupturing occurred causing a partially-and/or fully-opened lid features. The phase interface between La2O3 grains and W matrix was served as the nucleation sites for blistering and large-scale crack propagation near the surface. Small blisters were preferentially appeared on the grains with surface orientation of nearly (111) and that originated from the intra-granular crack at depths much closer to the sample surface. Micro-sized pits were formed on the WL10 surface after exposure to high fluence plasma, which was due to a higher sputtering rate of La2O3 grains during plasma exposure. For both materials, seeding He in D plasma can effectively inhibit the blister formation, and most serious blistering occurs with N seeding in D plasma. When exposed to Ar + D plasma, sparse small blisters were visible and most of blisters were ruptured for W, whereas there are some big blisters with long strip shape for WL10. The difference in blistering behavior between W and WL10 was attributed to the differences in microstructure, composition as well as ductility due to the presence of La2O3 phases. The sputtering yields increased slightly with He seeding in D plasma. N2 and Ar seeding in D plasma leaded to a significant increase in sputtering yields. As compared to the W, the WL10 exhibits a better sputtering erosion resistance in terms of the sputtering yield. The D retention in WL10 increases with D fluence and that was equal to or lower than that in W when exposed to the same conditions.(c) 2022 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.

Deuterium retention in tungsten and tungsten alloys exposed to pure and impurities seeding deuterium plasma

Erosion and deuterium retention behavior of tungsten exposed to impurity-seeded deuterium plasma

Blistering Behavior and Deuterium Retention in Tungsten Vanadium Alloys Exposed to Deuterium Plasma in the Linear Plasma Device STEP

Effects of Tantalum Alloying on Surface Morphology and Deuterium Retention in Tungsten Exposed to Deuterium Plasma

Deuterium retention in helium-irradiated tungsten

Deuterium behavior in tungsten exposed to deuterium plasma with rising or declining temperature

Deuterium Retention in Heavy-Ion and Helium-Ion Sequentially Irradiated Tungsten

Deuterium Retention in Tungsten-Doped Amorphous Carbon Films Exposed to Deuterium Plasma

Dependence of deuterium retention on helium ions irradiation in tungsten

Surface blistering and deuterium retention behaviors in pure and ZrC-doped tungsten exposed to deuterium plasma

The influence of impurities on the erosion of tungsten by low energy high flux deuterium plasma irradiation

Deuterium Retention in Tungsten Films Deposited by Magnetron Sputtering

Surface modification and deuterium retention of tungsten and tungsten-rhenium alloys exposed to deuterium plasma

Surface Modification and Deuterium Retention of High Energy Rate Forging W-Y2O3exposed to Deuterium Plasma

Influence of neon seeding on the deuterium retention and surface modification of ITER-like forged tungsten

Influence of impurity gas seeding into deuterium plasma on the surface modification, sputtering erosion and deuterium retention in W and W-La2O3 alloy

Tungsten fuzz annealing effect on deuterium retention in polycrystalline tungsten

Influence of Nitrogen Pre-Irradiation at Different Temperatures on Surface Blistering and Deuterium Retention in Tungsten

Blister-dominated retention mechanism in tungsten exposed to high-fluence deuterium plasma

Surface modification and deuterium retention in hot-rolled potassium doped tungsten alloy exposed to deuterium plasma

Deuterium retention in tungsten co-deposits with neon and argon inclusions