Abstract:Surface blistering and deuterium (D) retention of heavy ion pre-irradiated (1 dpa) tungsten (W) exposed to low-energy (40 eV) and high-flux (1-2 x 10(22) D/m(2)s) D plasma has been investigated with low fluence of 0.1 x 10(27) D/m(2) and a high fluence of 2.2 x 10(27) D/m(2). Surface morphology observations show that a large number of blisters are formed on the undamaged W after low-fluence exposure while the area density of the blister will have significantly increased and blister bursting will be triggered in the case of high-fluence exposure. In contrast, the heavy ion pre-irradiation noticeably reduces the area density of blisters for both low-and high-fluence exposures. The thermal desorption spectroscopy (TDS) shows that the total D retention in the pre-damaged W is greater than that of the undamaged sample, and this trend is more significant with increasing fluence/duration of D plasma exposure. The results of positron annihilation Doppler broadening spectrometry (PA-DBS) and TDS indicate that a large number of vacancy-type defects, especially those with a higher trapping energy of D, are induced by the heavy ion pre-irradiation. The increasing defects/D-trap sites may result in two outcomes, the D concentration will disperse at each blister nucleation site and D inward diffusion is enhanced and, therefore, lead to the mitigation of D-induced blistering and increase the D retention. In addition, combined with the enhanced D inward diffusion caused by increasing exposure duration, the D retention is therefore much higher in the pre-damaged W in the case of high-fluence exposure. (C) 2018 Elsevier B.V. All rights reserved.

Deuterium Retention in Heavy-Ion and Helium-Ion Sequentially Irradiated Tungsten

Deuterium retention in helium-irradiated tungsten

Dependence of deuterium retention on helium ions irradiation in tungsten

Comparing deuterium retention in heavy ion damaged tungsten measured by glow discharge optical emission spectroscopy, nuclear reaction analysis and thermal desorption spectroscopy

Irradiation hardening and deuterium retention behaviour of tungsten under synergistic irradiations of 3.5 MeV Fe 13+ ions and deuterium plasma

Effects of Deuterium Plasma Exposure and Helium Ions Irradiation on Nanoindentation Hardness of Tungsten

Reduced D Trapping by Plasma-Implanted He Nanobubbles in Radiation Damaged Tungsten

Deuterium retention in tungsten and tungsten alloys exposed to pure and impurities seeding deuterium plasma

Deuterium retention and thermal conductivity in ion-beam displacement-damaged tungsten

In situ measurements of low energy D plasma-driven permeation through He pre-damaged W

Microstructure Evolution and Effect on Deuterium Retention in Oxide Dispersion Strengthened Tungsten During He+ Irradiation

Microstructure Evolution and Effect on Deuterium Retention in TiC- and ZrC-Doped Tungsten under He+ Ion Irradiation

Dependence of blistering and deuterium retention on damage depth in damaged tungsten exposed to deuterium plasma

Effect of Heavy Ion Pre-Irradiation on Blistering and Deuterium Retention in Tungsten Exposed to High-Fluence Deuterium Plasma

Surface Modification and Deuterium Retention of High Energy Rate Forging W-Y2O3 Exposed to Deuterium Plasma

Effect of Surface Quality on Hydrogen/helium Irradiation Behavior in Tungsten

Temperature dependence of deuterium retention at displacement damage in tungsten

Microstructure and deuterium retention after ion irradiation of W–Lu2O3 composites

Behavior of helium cavities in ion-irradiated W-Ni-Fe ductile-phase toughened tungsten

Erosion and deuterium retention behavior of tungsten exposed to impurity-seeded deuterium plasma

Blistering Behavior and Deuterium Retention in Tungsten Vanadium Alloys Exposed to Deuterium Plasma in the Linear Plasma Device STEP