Abstract:Temperature is one of the critical factors that strongly affect the behavior of hydrogen isotopes in tungsten (W). This work investigates the effect of initial exposure temperature on the deuterium (D) retention and surface blistering in recrystallized W. D plasma exposure is started at 420 K and 600 K, respectively, and then changed to the same temperature of 520 K. For each temperature, the irradiation fluence is ∼ 1 × 1026 D m−2, and therefore the total fluence is ∼ 2 × 1026 D m−2 for each sample. A reference W sample was also exposed at 520 K with the same total fluence. Compared with the reference sample, it is found that the initial temperature of 420 K significantly inhibits the formation of intergranular blisters and leads to a reduction of intragranular blisters in size. Although the initial temperature of 600 K facilitates the formation of intergranular blisters, the intergranular blister size is reduced. This is possibly related to the relatively higher concentration of trapped D over a large depth range as revealed by the TMAP simulation results, leading to the fact that intergranular cracks are more prone to propagate along sloping grain boundaries. Thermal desorption spectra results show that the initial exposure temperature of 420 K and 600 K reduce D retention by a factor of ∼ 56 % and ∼ 34 %, respectively. It is considered to be connected with the blistering-induced defects and D transport in W, which are strongly affected by the initial exposure temperature. This work demonstrates that the initial exposure temperature plays a crucial role in D behavior in W, improving the understanding of the temperature effects of hydrogen isotopes behavior in W.

Deuterium Retention in Tungsten Films Deposited by Magnetron Sputtering

Deuterium Retention in Tungsten-Doped Amorphous Carbon Films Exposed to Deuterium Plasma

Deuterium retention in tungsten co-deposits with neon and argon inclusions

Effects of Tantalum Alloying on Surface Morphology and Deuterium Retention in Tungsten Exposed to Deuterium Plasma

Deuterium retention in tungsten and tungsten alloys exposed to pure and impurities seeding deuterium plasma

Surface morphology and deuterium retention in tungsten exposed to high flux D plasma at high temperatures

Surface blistering and deuterium retention behaviors in pure and ZrC-doped tungsten exposed to deuterium plasma

Blistering Behavior and Deuterium Retention in Tungsten Vanadium Alloys Exposed to Deuterium Plasma in the Linear Plasma Device STEP

Deuterium retention in helium-irradiated tungsten

Deuterium retention and thermal conductivity in ion-beam displacement-damaged tungsten

Blister-dominated retention mechanism in tungsten exposed to high-fluence deuterium plasma

Deuterium Blistering in Tungsten and Tungsten Vanadium Alloys

Erosion and deuterium retention behavior of tungsten exposed to impurity-seeded deuterium plasma

Deuterium retention and transport in ion-irradiated tungsten exposed to deuterium atoms: role of grain boundaries

Surface Blistering and Deuterium Retention in Chemical Vapor Deposition Tungsten Exposed to Deuterium Plasma

Surface modification and deuterium retention in hot-rolled potassium doped tungsten alloy exposed to deuterium plasma

Influence of nitrogen pre-implantation on deuterium retention in tungsten

Surface Modification and Deuterium Retention of High Energy Rate Forging W-Y2O3 Exposed to Deuterium Plasma

Tungsten fuzz annealing effect on deuterium retention in polycrystalline tungsten

Characterization on deuterium retention in tungsten target using spatially resolved laser induced desorption-quadrupole mass spectroscopy

Effect of initial exposure temperature on the deuterium retention and surface blistering in tungsten