CdS/CdSO 4 Nanoflower-Based Photodetector with Enhanced Photoelectric Performances
Ziliang Li,Fatemeh Davar,Jiaxin Chen,Ziqing Li,Xiaosheng Fang
DOI: https://doi.org/10.1021/acsanm.0c02166
IF: 6.14
2020-09-21
ACS Applied Nano Materials
Abstract:Effective engineering of materials with distinctive nanoscale microstructures provides lots of opportunities to explore their underlying photoelectric phenomena deeply. Here, the microstructural and photoelectric characteristics of a CdS/CdSO<sub>4</sub> flower-like nanostructure (nanoflower) prepared by a simple chemical route and a following thermal treatment were investigated. A hybrid composition of cubic CdS, hexagonal CdS, and CdSO<sub>4</sub> phases was obtained when the thermal annealing was conducted at 480 °C. The conductivity of CdS/CdSO<sub>4</sub> nanoflowers was significantly enhanced compared with that of pristine CdS nanoflowers, giving excellent photoelectric performances, such as high photocurrent (∼0.2 μA), photoresponse speed (<i>t</i><sub>rise</sub> = 2.8 ms, <i>t</i><sub>fall</sub> = 14.4 ms), photoresponsivity (∼0.3 A/W), and detectivity (∼6 × 10<sup>9</sup> Jones). The conductivity gain and substantially high photoresponse speed originated from the improved crystallinity and the realization of a special microstructural defect landscape within the nanoflowers, enriching the photoelectric behavior of CdS series materials as well as the development of low-dimensional optoelectronic devices operating in a large wavelength region.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsanm.0c02166?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsanm.0c02166</a>.FE-SEM images of the 480 °C treated CdS nanoflowers after ultrasonic treatment; XRD pattern of the as-prepared CdS nanoflower powders; XPS survey scan of the as-prepared, 400 and 480 °C thermally treated nanoflowers; PL spectra of the as-prepared CdS nanoflowers measured under an excitation wavelength of 340 nm; photograph of the 480 °C treated nanoflower-based PD with detailed size marking of the conducting channel; <i>I</i>–<i>V</i> curves of the 300, 400, and 480 °C treated nanoflower-based PDs measured under dark and 300–650 nm light illuminations; and comparison of the on/off switching behaviors of the PD measured with different humidities (<a class="ext-link" href="/doi/suppl/10.1021/acsanm.0c02166/suppl_file/an0c02166_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology