Homogeneously-Alloyed CdTeSe Single-Sized Nanocrystals with Bandgap Photoluminescence
Ruibing Wang,Olivier Calvignanello,Christopher I. Ratcliffe,Xiaohua Wu,Donald M. Leek,Md. Badruz Zaman,David Kingston,John A. Ripmeester,Kui Yu
DOI: https://doi.org/10.1021/jp810325z
2009-01-01
Abstract:Homogeneously alloyed ternary CdTeSe magic-sized nanocrystals (MSNs) with bandgap emission were synthesized in I-octadecene (ODE) via a noninjection one-pot approach featuring synthetic reproducibility and large-scale capability. The noninjection approach used cadmium acetate dihydrate (Cd(OAc)(2)center dot 2H(2)O), elemental selenium, and elemental tellurium as Cd, Se, and Te sources, respectively. The growth of the CdTeSe nanocrystals was carried out at temperatures from 120 to 200 degrees C for several hours in a reaction flask containing the reactants together with a long-chain fatty acid as capping ligands and ODE as the reaction medium. During synthesis, the CdTeSe nanocrystals exhibited persistent bandgap and did not grow in size anymore after their formation, either with longer growth periods or higher reaction temperature. Also, they exhibit an absorption doublet with 288 meV energy difference between the two peaks; the first excitonic transition peak is at 520 nm and bandgap photoemission peak at 524 nm with full width at half-maximum (fwhm) of ca. 20 nm. Both the growth pattern and the optical properties suggest that they are magic-sized and thus termed as single-sized. Nuclear magnetic resonance (NMR), with sensitivity to local environment, provided valuable information regarding the structure and composition of the nanocrystals. Solid-state C-13 cross polarization/magic angle spinning (CP/MAS) NMR spectra showed that the carboxylate capping ligand is firmly attached to the crystal, and H-1 decoupled Cd-113 MAS spectra, with and without CP, distinguished between the surface Cd species and the Cd inside a nanocrystal. The Cd-113 NMR results also confirmed, unambiguously, that the nanocrystals are homogeneously alloyed ternary CdTeSe, with Cd-113 resonances located between those of CdTe and CdSe nanocrystals indicating a stoichiometry of approximately I Se: ITe ratio throughout the whole nanocrystal. XRD supported that they are ternary-alloyed CdTeSe rather than binary CdTe or CdSe, with a wurtzite crystal structure. In addition, both energy-dispersive X-ray spectroscopy (EDX) and X-ray photoelectron spectroscopy (XPS) supported an approximate stoichiometric ratio of ISe:ITe of the CdTeSe nanocrystals.